General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 0.9 g/cm³ Show Material materials with Density of 0.9 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 700 % Show Material materials with Elongation of 700 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 0.25 GPa Show Material materials with Flexural modulus of 0.25 GPa | ISO 178 |
Hardness, Shore D | 23.0 °C | 42 [-] Show Material materials with Hardness, Shore D of 42 [-] | ISO 7619-1 | 15 seconds |
Tear strength | 23.0 °C | 100 kN/m Show Material materials with Tear strength of 100 kN/m | ISO 34-1 |
Tensile strength | 23.0 °C | 24 MPa Show Material materials with Tensile strength of 24 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.2E-6 1/K Show Material materials with Coefficient of thermal expansion of 1.2E-6 1/K | ISO 11359-1/-2 |
Coefficient of thermal expansion, transverse | 23.0 °C | 2.7E-6 1/K Show Material materials with Coefficient of thermal expansion, transverse of 2.7E-6 1/K | ISO 11359-1/-2 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 65°C, Drying Time, Dehumidified Dryer: 2-4h, Melt Temperature Optimum: 280°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 25°C, Max. mold temperature: 60°C |