General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.18 g/cm³ Show Material materials with Density of 1.18 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Compression set | 23.0 °C | 22 [-] Show Material materials with Compression set of 22 [-] | ISO 815 |
70.0 °C | 75 [-] Show Material materials with Compression set of 75 [-] | ISO 815 | |
Elongation | 23.0 °C | 554 % Show Material materials with Elongation of 554 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 0.03 GPa Show Material materials with Flexural modulus of 0.03 GPa | ISO 178 |
Flexural strength | 23.0 °C | 2.4 MPa Show Material materials with Flexural strength of 2.4 MPa | ISO 178 |
Hardness, Shore A | 23.0 °C | 73 [-] Show Material materials with Hardness, Shore A of 73 [-] | ISO 7619-1 | 3 seconds |
Tear strength, transverse | 23.0 °C | 48.6 kN/m Show Material materials with Tear strength, transverse of 48.6 kN/m | ISO 34-1 |
Tensile strength | 23.0 °C | 14.5 MPa Show Material materials with Tensile strength of 14.5 MPa | ISO 527-1/-2 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 27 g/10min Show Material materials with Melt mass-flow rate of 27 g/10min | ISO 1133 | 230°C/10kg | |
Shrinkage | 23.0 °C | 2 % Show Material materials with Shrinkage of 2 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 70°C, Drying Time, Dehumidified Dryer: 2-4h, Melt Temperature Optimum: 195°C, Max. screw tangential speed: 0.4m/s, Mold Temperature Optimum: 30°C, Min. mold temperature: 20°C, Max. mold temperature: 40°C |