General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 0.9 g/cm³ Show Material materials with Density of 0.9 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 400 % Show Material materials with Elongation of 400 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 0.41 GPa Show Material materials with Flexural modulus of 0.41 GPa | ISO 178 |
Tensile strength | 23.0 °C | 19 MPa Show Material materials with Tensile strength of 19 MPa | ISO 527-1/-2 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 11 g/10min Show Material materials with Melt mass-flow rate of 11 g/10min | ISO 1133 | 230°C/2.16kg | |
Shrinkage | 23.0 °C | 0.7 % Show Material materials with Shrinkage of 0.7 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 65°C, Drying Time, Dehumidified Dryer: 2-4h, Melt Temperature Optimum: 225°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 35°C, Max. mold temperature: 50°C |