Hytrel® HTR8351 NC021

Alternative and trade names
TPC-ET
Want to keep this datasheet? Save it now in your required format

Description

Common features of Hytrel® thermoplastic polyester elastomer include mechanical and physical properties such as exceptional toughness and resilience, high resistance to creep, impact and flex fatigue, flexibility at low temperatures and good retention of properties at elevated temperatures. In addition, it resists many industrial chemicals, oils and solvents. Special grades include heat stabilised, flame retardant, food contact compliant, blow molding and extrusion grades. Concentrates offered include black pigments, UV protection additives, heat stabilisers, and flame retardants. Hytrel® thermoplastic polyester elastomer is plasticiser free.The good melt stability of Hytrel® thermoplastic polyester elastomer normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-24 kJ/g of base polymer) in appropriately equipped installations.For disposal, local regulations have to be observed. Hytrel® thermoplastic polyester elastomer typically is used in demanding applications in the automotive, fluid power, electrical/electronic, consumer goods, appliance and power tool, sporting goods, furniture, industrial and off-road transportation/equipment industry.Hytrel®HTR8351 NC021is a low modulus Hytrel® grade with nominal durometer hardness of 30D. Itis a non-discoloring, UV stabilized, plasticizer free resin for extrusion. Typical applications: Wire and cable jackets.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.15 g/cm³

Show Material materials with Density of 1.15 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

0.02 GPa

Show Material materials with Elastic modulus of 0.02 GPa

ISO 527-1/-2

Elongation

23.0 °C

210 %

Show Material materials with Elongation of 210 %

ISO 527-1/-2

Hardness, Shore D

23.0 °C

21 [-]

Show Material materials with Hardness, Shore D of 21 [-]

ISO 7619-1 | 15 seconds

Impact strength, Charpy notched

-40.0 °C

4 kJ/m²

Show Material materials with Impact strength, Charpy notched of 4 kJ/m²

ISO 179/1eA

-6.0 °C

13 kJ/m²

Show Material materials with Impact strength, Charpy notched of 13 kJ/m²

ISO 179/1eA

Tear strength, transverse

23.0 °C

54 kN/m

Show Material materials with Tear strength, transverse of 54 kN/m

ISO 34-1

Tensile strength

23.0 °C

9 MPa

Show Material materials with Tensile strength of 9 MPa

ISO 527-1/-2

Thermal

PropertyValueComment

Melting point

160 °C

Show Material materials with Melting point of 160 °C

ISO 11357-1/-3 | 18°F/min

Vicat softening temperature

47 °C

Show Material materials with Vicat softening temperature of 47 °C

ISO 306 | 90°F, 2 lbf

Flammability

FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

10 g/10min

Show Material materials with Melt mass-flow rate of 10 g/10min

ISO 1133 | 190°C/5kg

Shrinkage

23.0 °C

0.7 %

Show Material materials with Shrinkage of 0.7 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

0.5 %

Show Material materials with Shrinkage, transverse of 0.5 %

ISO 294-4, 2577

Technological properties

Property
Processing methods

Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 190°C, Min. melt temperature: 180°C, Max. melt temperature: 200°C, Mold Temperature Optimum: 30°C, Min. mold temperature: 30°C, Max. mold temperature: 40°C