General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.19 g/cm³ Show Material materials with Density of 1.19 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.19 GPa Show Material materials with Elastic modulus of 0.19 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 450 % Show Material materials with Elongation of 450 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 0.19 GPa Show Material materials with Flexural modulus of 0.19 GPa | ISO 178 | ||
Hardness, Shore D | 23.0 °C | 56 [-] Show Material materials with Hardness, Shore D of 56 [-] | max., ISO 7619-1 | ||
Impact strength, Charpy notched | -40.0 °C | 19 kJ/m² Show Material materials with Impact strength, Charpy notched of 19 kJ/m² | No Break @ 23°C, ISO 179/1eU | ||
-6.0 °C | 39 kJ/m² Show Material materials with Impact strength, Charpy notched of 39 kJ/m² | No Break @ 23°C, ISO 179/1eU | |||
Impact strength, Izod unnotched | -40.0 °C | 20 kJ/m² Show Material materials with Impact strength, Izod unnotched of 20 kJ/m² | ISO 180/1A | ||
Poisson's ratio | 23.0 °C | 0.48 [-] Show Material materials with Poisson's ratio of 0.48 [-] | |||
Tear strength | 23.0 °C | 150 kN/m Show Material materials with Tear strength of 150 kN/m | ISO 34-1 | ||
Tear strength, transverse | 23.0 °C | 135 kN/m Show Material materials with Tear strength, transverse of 135 kN/m | ISO 34-1 | ||
Tensile strength | 23.0 °C | 38 MPa Show Material materials with Tensile strength of 38 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23°C, ISO 179/1eU |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -54 °C Show Material materials with Brittleness temperature of -54 °C | ISO 974 | |||
Glass transition temperature | -40 °C Show Material materials with Glass transition temperature of -40 °C | ISO 11357-1/-2 | 18°F/min | |||
Melting point | 214 °C Show Material materials with Melting point of 214 °C | ISO 11357-1/-3 | 18°F/min | |||
Specific heat capacity | 23.0 °C | 2150 J/(kg·K) Show Material materials with Specific heat capacity of 2150 J/(kg·K) | of melt | ||
Vicat softening temperature | 182 °C Show Material materials with Vicat softening temperature of 182 °C | ISO 306 | 90°F, 2 lbf | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: 42 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 9 g/10min Show Material materials with Melt mass-flow rate of 9 g/10min | ISO 1133 | 240°C/10kg | |
Melt volume-flow rate | 9 cm³/10min Show Material materials with Melt volume-flow rate of 9 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 2.2 % Show Material materials with Shrinkage of 2.2 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 2.1 % Show Material materials with Shrinkage, transverse of 2.1 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 245°C, Min. melt temperature: 240°C, Max. melt temperature: 255°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 55°C |