MULTIFLEX™ TPO 4203 SI1 NAT 26219

Want to keep this datasheet? Save it now in your required format

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

0.89 g/cm³

Show Material materials with Density of 0.89 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

110 %

Show Material materials with Elongation of 110 %

ISO 527-1/-2

Flexural modulus

23.0 °C

0.42 GPa

Show Material materials with Flexural modulus of 0.42 GPa

ISO 178

Hardness, Shore D

23.0 °C

38 [-]

Show Material materials with Hardness, Shore D of 38 [-]

ISO 7619-1 | 15 seconds

Impact strength, Izod unnotched

-50.0 °C

55 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 55 kJ/m²

ISO 180/1A

Tear strength

23.0 °C

96 kN/m

Show Material materials with Tear strength of 96 kN/m

ISO 34-1

Tensile strength

23.0 °C

16 MPa

Show Material materials with Tensile strength of 16 MPa

ISO 527-1/-2

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

7 cm³/10min

Show Material materials with Melt volume-flow rate of 7 cm³/10min

ISO 1133

Shrinkage

23.0 °C

1 %

Show Material materials with Shrinkage of 1 %

ISO 294-4, 2577

Technological properties

Property
Processing methods

Drying Recommended: no, Melt Temperature Optimum: 235°C, Mold Temperature Optimum: 30°C, Min. mold temperature: 20°C, Max. mold temperature: 40°C, Hold pressure range: as low as possible, Back pressure: 1MPa