General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 0.89 g/cm³ Show Material materials with Density of 0.89 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 260 % Show Material materials with Elongation of 260 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 0.25 GPa Show Material materials with Flexural modulus of 0.25 GPa | ISO 178 |
Hardness, Shore D | 23.0 °C | 34 [-] Show Material materials with Hardness, Shore D of 34 [-] | ISO 7619-1 | 15 seconds |
Impact strength, Izod unnotched | -50.0 °C | 74 kJ/m² Show Material materials with Impact strength, Izod unnotched of 74 kJ/m² | ISO 180/1A |
Tear strength | 23.0 °C | 76 kN/m Show Material materials with Tear strength of 76 kN/m | ISO 34-1 |
Tensile strength | 23.0 °C | 13 MPa Show Material materials with Tensile strength of 13 MPa | ISO 527-1/-2 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 5 cm³/10min Show Material materials with Melt volume-flow rate of 5 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.5 % Show Material materials with Shrinkage of 1.5 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Color | Black | |
Processing methods | Drying Recommended: yes, Drying Temperature: 60°C, Drying Time, Dehumidified Dryer: 2-4h, Melt Temperature Optimum: 245°C, Mold Temperature Optimum: 30°C, Min. mold temperature: 20°C, Max. mold temperature: 40°C, Hold pressure range: as low as possible, Back pressure: 1MPa |