MULTIFLEX™ TEO 3503 S1 BLK 21152

Want to keep this datasheet? Save it now in your required format

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts





23.0 °C

0.88 g/cm³

Show Material materials with Density of 0.88 g/cm³

ISO 1183




23.0 °C

150 %

Show Material materials with Elongation of 150 %

ISO 527-1/-2

Flexural modulus

23.0 °C

0.42 GPa

Show Material materials with Flexural modulus of 0.42 GPa

ISO 178

Hardness, Shore D

23.0 °C

43 [-]

Show Material materials with Hardness, Shore D of 43 [-]

ISO 7619-1 | 15 seconds

Impact strength, Izod unnotched

-30.0 °C

68 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 68 kJ/m²

ISO 180/1A

Tear strength

23.0 °C

88 kN/m

Show Material materials with Tear strength of 88 kN/m

ISO 34-1

Tensile strength

23.0 °C

13 MPa

Show Material materials with Tensile strength of 13 MPa

ISO 527-1/-2

Rheological Properties


Melt volume-flow rate

10 cm³/10min

Show Material materials with Melt volume-flow rate of 10 cm³/10min

ISO 1133


23.0 °C

1.2 %

Show Material materials with Shrinkage of 1.2 %

ISO 294-4, 2577

Technological properties



Processing methods

Drying Recommended: no, Melt Temperature Optimum: 245°C, Mold Temperature Optimum: 30°C, Min. mold temperature: 20°C, Max. mold temperature: 40°C, Hold pressure range: as low as possible, Back pressure: 1MPa