Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.16 g/cm³ Show Material materials with Density of 1.16 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 0.27 GPa Show Material materials with Elastic modulus of 0.27 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 300 % Show Material materials with Elongation of 300 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 0.27 GPa Show Material materials with Flexural modulus of 0.27 GPa | ISO 178 |
Hardness, Shore D | 23.0 °C | 60 [-] Show Material materials with Hardness, Shore D of 60 [-] | max., ISO 7619-1 |
Impact strength, Charpy notched | -40.0 °C | 7 kJ/m² Show Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO 179/1eA |
-6.0 °C | 12 kJ/m² Show Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA | |
23.0 °C | 102 kJ/m² Show Material materials with Impact strength, Charpy notched of 102 kJ/m² | ISO 179/1eA | |
Impact strength, Izod unnotched | -40.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod unnotched of 7 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.48 [-] Show Material materials with Poisson's ratio of 0.48 [-] | |
Tear strength | 23.0 °C | 140 kN/m Show Material materials with Tear strength of 140 kN/m | ISO 34-1 |
Tear strength, transverse | 23.0 °C | 130 kN/m Show Material materials with Tear strength, transverse of 130 kN/m | ISO 34-1 |
Tensile strength | 23.0 °C | 33 MPa Show Material materials with Tensile strength of 33 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -65 °C Show Material materials with Brittleness temperature of -65 °C | ISO 974 | |||
Coefficient of thermal expansion | 23.0 °C | 2E-4 1/K Show Material materials with Coefficient of thermal expansion of 2E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.8E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.8E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Glass transition temperature | 15 °C Show Material materials with Glass transition temperature of 15 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 65 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 65 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 45 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 45 °C | ISO 75-1/-2 | |||
Melting point | 215 °C Show Material materials with Melting point of 215 °C | ISO 11357-1/-3 | 18°F/min | |||
Vicat softening temperature | 195 °C Show Material materials with Vicat softening temperature of 195 °C | ISO 306 | 90°F, 2 lbf | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 4 g/10min Show Material materials with Melt mass-flow rate of 4 g/10min | ISO 1133 | 240°C/10kg | |
Shrinkage | 23.0 °C | 2.4 % Show Material materials with Shrinkage of 2.4 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 2.2 % Show Material materials with Shrinkage, transverse of 2.2 % | ISO 294-4, 2577 |
Technological properties
Property |
---|