Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa | Typical for Wrought Copper High Copper Alloy |
Elongation A50 | 23.0 °C | 2 - 8 % Show Material materials with Elongation A50 of 2 - 8 % | |
Hardness, Rockwell B | 23.0 °C | 88 - 104 [-] Show Material materials with Hardness, Rockwell B of 88 - 104 [-] | |
Hardness, Rockwell Superficial 15-T | 23.0 °C | 90 - 94 [-] Show Material materials with Hardness, Rockwell Superficial 15-T of 90 - 94 [-] | |
Hardness, Rockwell Superficial 30-T | 23.0 °C | 77 - 83 [-] Show Material materials with Hardness, Rockwell Superficial 30-T of 77 - 83 [-] | |
Tensile strength | 23.0 °C | 585 - 895 MPa Show Material materials with Tensile strength of 585 - 895 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K | Typical for Wrought Copper High Copper Alloy |
Melting point | 855 - 1090 °C Show Material materials with Melting point of 855 - 1090 °C | Typical for Wrought Copper High Copper Alloy | |
Specific heat capacity | 23.0 °C | 360 - 420 J/(kg·K) Show Material materials with Specific heat capacity of 360 - 420 J/(kg·K) | Typical for Wrought Copper High Copper Alloy |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.2 % Show Material materials with Aluminium of 0.2 % |
Beryllium | 1.6 - 1.85 % Show Material materials with Beryllium of 1.6 - 1.85 % |
Silicon | 0.2 % Show Material materials with Silicon of 0.2 % |