Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa | Typical for Wrought Copper High Copper Alloy |
Elongation A50 | 23.0 °C | 15 % Show Material materials with Elongation A50 of 15 % | |
Hardness, Rockwell C | 23.0 °C | 20 [-] Show Material materials with Hardness, Rockwell C of 20 [-] | |
Hardness, Rockwell Superficial 15-N | 23.0 °C | 70 [-] Show Material materials with Hardness, Rockwell Superficial 15-N of 70 [-] | |
Hardness, Rockwell Superficial 30-N | 23.0 °C | 42 [-] Show Material materials with Hardness, Rockwell Superficial 30-N of 42 [-] | |
Tensile strength | 23.0 °C | 760 - 825 MPa Show Material materials with Tensile strength of 760 - 825 MPa | |
Yield strength | 23.0 °C | 550 - 760 MPa Show Material materials with Yield strength of 550 - 760 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K | Typical for Wrought Copper High Copper Alloy |
Melting point | 855 - 1090 °C Show Material materials with Melting point of 855 - 1090 °C | Typical for Wrought Copper High Copper Alloy | |
Specific heat capacity | 23.0 °C | 360 - 420 J/(kg·K) Show Material materials with Specific heat capacity of 360 - 420 J/(kg·K) | Typical for Wrought Copper High Copper Alloy |