Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 8.47 g/cm³ Show Material materials with Density of 8.47 g/cm³ | Typical for Cast Copper Brass Yellow Brass |
Grain size | 0.0307 μm Show Material materials with Grain size of 0.0307 μm | Predicted Value |
Mechanical
| Property | Value | Related Standards | Shape | Comment |
|---|---|---|---|---|
Compressive strength | 1151 MPa Show Material materials with Compressive strength of 1151 MPa | Predicted Value | ||
Elastic modulus | 110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa | Typical for Cast Copper Brass Yellow Brass | ||
Fatigue strength | 378 MPa Show Material materials with Fatigue strength of 378 MPa | Predicted Value | ||
Hardness, Brinell | 162 [-] Show Material materials with Hardness, Brinell of 162 [-] | Predicted Value | ||
Hardness, HBW | 237.8 [-] Show Material materials with Hardness, HBW of 237.8 [-] | Predicted Value | ||
Hardness, Rockwell F | 78 [-] Show Material materials with Hardness, Rockwell F of 78 [-] | Predicted Value | ||
Hardness, Rockwell Superficial 15-N | 70 [-] Show Material materials with Hardness, Rockwell Superficial 15-N of 70 [-] | Predicted Value | ||
Hardness, Rockwell Superficial 30-N | 42 [-] Show Material materials with Hardness, Rockwell Superficial 30-N of 42 [-] | Predicted Value | ||
Hardness, Rockwell Superficial 30-T | 78 [-] Show Material materials with Hardness, Rockwell Superficial 30-T of 78 [-] | Predicted Value | ||
Hardness, Vickers | 141 [-] Show Material materials with Hardness, Vickers of 141 [-] | Predicted Value | ||
Poisson's ratio | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | Typical for Cast Copper Brass Yellow Brass | ||
Reduction of area | 35.8 % Show Material materials with Reduction of area of 35.8 % | Predicted Value | ||
Shear modulus | 43.7 GPa Show Material materials with Shear modulus of 43.7 GPa | Predicted Value | ||
Shear strength | 366 MPa Show Material materials with Shear strength of 366 MPa | Predicted Value | ||
Tensile strength | 621 MPa Show Material materials with Tensile strength of 621 MPa | ASTM B505 | Casting |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.5e-05 - 1.9e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.5e-05 - 1.9e-05 1/K | Typical for Cast Copper Brass Yellow Brass |
Melting point | 905 - 932 °C Show Material materials with Melting point of 905 - 932 °C | Typical for Cast Copper Brass Yellow Brass |
Specific heat capacity | 335 - 390 J/(kg·K) Show Material materials with Specific heat capacity of 335 - 390 J/(kg·K) | Typical for Cast Copper Brass Yellow Brass |
Thermal conductivity | 116 W/(m·K) Show Material materials with Thermal conductivity of 116 W/(m·K) | Typical for Cast Copper Brass Yellow Brass |
Electrical
Chemical properties
| Property | Value | Related Standards | Shape |
|---|---|---|---|
Aluminium | 3 - 4.9 % Show Material materials with Aluminium of 3 - 4.9 % | ASTM B505 | Casting |
Copper | 60 - 66 % Show Material materials with Copper of 60 - 66 % | ASTM B505 | Casting |
Iron | 2 - 4 % Show Material materials with Iron of 2 - 4 % | ASTM B505 | Casting |
Lead | 0.2 % Show Material materials with Lead of 0.2 % | ASTM B505 | Casting |
Manganese | 2.5 - 5 % Show Material materials with Manganese of 2.5 - 5 % | ASTM B505 | Casting |
Nickel | 1 % Show Material materials with Nickel of 1 % | ASTM B505 | Casting |
Tin | 0.2 % Show Material materials with Tin of 0.2 % | ASTM B505 | Casting |
Zinc | 22 - 28 % Show Material materials with Zinc of 22 - 28 % | ASTM B505 | Casting |