General
Property | Value | Comment |
---|---|---|
Density | 7.631 g/cm³ Show Material materials with Density of 7.631 g/cm³ | Predicted Value |
Grain size | 0.031 μm Show Material materials with Grain size of 0.031 μm | Predicted Value |
Mechanical
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Compressive strength | 1184 MPa Show Material materials with Compressive strength of 1184 MPa | Predicted Value | |||
Elastic modulus | 96 - 120 GPa Show Material materials with Elastic modulus of 96 - 120 GPa | Typical for Cast Copper Bronze | |||
Fatigue strength | 380 MPa Show Material materials with Fatigue strength of 380 MPa | Predicted Value | |||
Hardness, Brinell | 183 [-] Show Material materials with Hardness, Brinell of 183 [-] | Predicted Value | |||
Hardness, HBW | 237.8 [-] Show Material materials with Hardness, HBW of 237.8 [-] | Predicted Value | |||
Hardness, Rockwell F | 79 [-] Show Material materials with Hardness, Rockwell F of 79 [-] | Predicted Value | |||
Hardness, Rockwell Superficial 15-N | 73 [-] Show Material materials with Hardness, Rockwell Superficial 15-N of 73 [-] | Predicted Value | |||
Hardness, Rockwell Superficial 30-N | 46 [-] Show Material materials with Hardness, Rockwell Superficial 30-N of 46 [-] | Predicted Value | |||
Hardness, Rockwell Superficial 30-T | 78 [-] Show Material materials with Hardness, Rockwell Superficial 30-T of 78 [-] | Predicted Value | |||
Hardness, Vickers | 203 [-] Show Material materials with Hardness, Vickers of 203 [-] | Predicted Value | |||
Poisson's ratio | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | Typical for Cast Copper Bronze | |||
Reduction of area | 36.5 % Show Material materials with Reduction of area of 36.5 % | Predicted Value | |||
Shear modulus | 46.2 GPa Show Material materials with Shear modulus of 46.2 GPa | Predicted Value | |||
Shear strength | 368.5 MPa Show Material materials with Shear strength of 368.5 MPa | Predicted Value | |||
Tensile strength | 655 MPa Show Material materials with Tensile strength of 655 MPa | Heat-Treated | ASTM B505 | Casting |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 1.9e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.6e-05 - 1.9e-05 1/K | Typical for Cast Copper Bronze |
Melting point | 760 - 1060 °C Show Material materials with Melting point of 760 - 1060 °C | Typical for Cast Copper Bronze |
Specific heat capacity | 376 - 440 J/(kg·K) Show Material materials with Specific heat capacity of 376 - 440 J/(kg·K) | Typical for Cast Copper Bronze |
Thermal conductivity | 12 - 81 W/(m·K) Show Material materials with Thermal conductivity of 12 - 81 W/(m·K) | Typical for Cast Copper Bronze |
Electrical
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 10 - 11.5 % Show Material materials with Aluminium of 10 - 11.5 % | Heat-Treated | ASTM B505 | Casting |
Copper | 78 % Show Material materials with Copper of 78 % | Heat-Treated | ASTM B505 | Casting |
Iron | 3 - 5 % Show Material materials with Iron of 3 - 5 % | Heat-Treated | ASTM B505 | Casting |
Manganese | 3.5 % Show Material materials with Manganese of 3.5 % | Heat-Treated | ASTM B505 | Casting |
Nickel | 3 - 5.5 % Show Material materials with Nickel of 3 - 5.5 % | Heat-Treated | ASTM B505 | Casting |