General
Property | Value | Comment |
---|---|---|
Density | 7.681 g/cm³ Show Material materials with Density of 7.681 g/cm³ | Predicted Value |
Grain size | 0.0314 μm Show Material materials with Grain size of 0.0314 μm | Predicted Value |
Mechanical
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Compressive strength | 1183 MPa Show Material materials with Compressive strength of 1183 MPa | Predicted Value | |||
Elastic modulus | 96 - 120 GPa Show Material materials with Elastic modulus of 96 - 120 GPa | Typical for Cast Copper Bronze | |||
Fatigue strength | 382 MPa Show Material materials with Fatigue strength of 382 MPa | Predicted Value | |||
Hardness, Brinell | 184 [-] Show Material materials with Hardness, Brinell of 184 [-] | Predicted Value | |||
Hardness, HBW | 241.5 [-] Show Material materials with Hardness, HBW of 241.5 [-] | Predicted Value | |||
Hardness, Rockwell F | 79 [-] Show Material materials with Hardness, Rockwell F of 79 [-] | Predicted Value | |||
Hardness, Rockwell Superficial 15-N | 73 [-] Show Material materials with Hardness, Rockwell Superficial 15-N of 73 [-] | Predicted Value | |||
Hardness, Rockwell Superficial 30-N | 46 [-] Show Material materials with Hardness, Rockwell Superficial 30-N of 46 [-] | Predicted Value | |||
Hardness, Rockwell Superficial 30-T | 81 [-] Show Material materials with Hardness, Rockwell Superficial 30-T of 81 [-] | Predicted Value | |||
Hardness, Vickers | 199 [-] Show Material materials with Hardness, Vickers of 199 [-] | Predicted Value | |||
Poisson's ratio | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | Typical for Cast Copper Bronze | |||
Reduction of area | 34.0 % Show Material materials with Reduction of area of 34.0 % | Predicted Value | |||
Shear modulus | 45.5 GPa Show Material materials with Shear modulus of 45.5 GPa | Predicted Value | |||
Shear strength | 346.2 MPa Show Material materials with Shear strength of 346.2 MPa | Predicted Value | |||
Tensile strength | 758 MPa Show Material materials with Tensile strength of 758 MPa | HT, Heat-Treated | ASTM B505 | Casting |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 1.9e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.6e-05 - 1.9e-05 1/K | Typical for Cast Copper Bronze |
Melting point | 760 - 1060 °C Show Material materials with Melting point of 760 - 1060 °C | Typical for Cast Copper Bronze |
Specific heat capacity | 376 - 440 J/(kg·K) Show Material materials with Specific heat capacity of 376 - 440 J/(kg·K) | Typical for Cast Copper Bronze |
Thermal conductivity | 12 - 81 W/(m·K) Show Material materials with Thermal conductivity of 12 - 81 W/(m·K) | Typical for Cast Copper Bronze |
Electrical
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 10 - 11.5 % Show Material materials with Aluminium of 10 - 11.5 % | HT, Heat-Treated | ASTM B505 | Casting |
Copper | 78 % Show Material materials with Copper of 78 % | HT, Heat-Treated | ASTM B505 | Casting |
Iron | 3 - 5 % Show Material materials with Iron of 3 - 5 % | HT, Heat-Treated | ASTM B505 | Casting |
Manganese | 3.5 % Show Material materials with Manganese of 3.5 % | HT, Heat-Treated | ASTM B505 | Casting |
Nickel | 3 - 5.5 % Show Material materials with Nickel of 3 - 5.5 % | HT, Heat-Treated | ASTM B505 | Casting |