General
Property | Value | Comment |
---|---|---|
Density | 8.47 g/cm³ Show Material materials with Density of 8.47 g/cm³ | Typical for Cast Copper Brass Yellow Brass |
Grain size | 0.0306 μm Show Material materials with Grain size of 0.0306 μm | Predicted Value |
Mechanical
Property | Value | Related Standards | Shape | Comment |
---|---|---|---|---|
Compressive strength | 1154 MPa Show Material materials with Compressive strength of 1154 MPa | Predicted Value | ||
Elastic modulus | 110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa | Typical for Cast Copper Brass Yellow Brass | ||
Fatigue strength | 379 MPa Show Material materials with Fatigue strength of 379 MPa | Predicted Value | ||
Hardness, Brinell | 146 [-] Show Material materials with Hardness, Brinell of 146 [-] | Predicted Value | ||
Hardness, HBW | 243.2 [-] Show Material materials with Hardness, HBW of 243.2 [-] | Predicted Value | ||
Hardness, Rockwell F | 78 [-] Show Material materials with Hardness, Rockwell F of 78 [-] | Predicted Value | ||
Hardness, Rockwell Superficial 15-N | 71 [-] Show Material materials with Hardness, Rockwell Superficial 15-N of 71 [-] | Predicted Value | ||
Hardness, Rockwell Superficial 30-N | 43 [-] Show Material materials with Hardness, Rockwell Superficial 30-N of 43 [-] | Predicted Value | ||
Hardness, Rockwell Superficial 30-T | 75 [-] Show Material materials with Hardness, Rockwell Superficial 30-T of 75 [-] | Predicted Value | ||
Hardness, Vickers | 143 [-] Show Material materials with Hardness, Vickers of 143 [-] | Predicted Value | ||
Poisson's ratio | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | Typical for Cast Copper Brass Yellow Brass | ||
Reduction of area | 36.4 % Show Material materials with Reduction of area of 36.4 % | Predicted Value | ||
Shear modulus | 42.9 GPa Show Material materials with Shear modulus of 42.9 GPa | Predicted Value | ||
Shear strength | 313.3 MPa Show Material materials with Shear strength of 313.3 MPa | Predicted Value | ||
Tensile strength | 552 MPa Show Material materials with Tensile strength of 552 MPa | ASTM B584 | Casting |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 1.5e-05 - 1.9e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.5e-05 - 1.9e-05 1/K | Typical for Cast Copper Brass Yellow Brass |
Melting point | 905 - 932 °C Show Material materials with Melting point of 905 - 932 °C | Typical for Cast Copper Brass Yellow Brass |
Specific heat capacity | 335 - 390 J/(kg·K) Show Material materials with Specific heat capacity of 335 - 390 J/(kg·K) | Typical for Cast Copper Brass Yellow Brass |
Thermal conductivity | 116 W/(m·K) Show Material materials with Thermal conductivity of 116 W/(m·K) | Typical for Cast Copper Brass Yellow Brass |
Electrical
Chemical properties
Property | Value | Related Standards | Shape |
---|---|---|---|
Aluminium | 1 - 3 % Show Material materials with Aluminium of 1 - 3 % | ASTM B584 | Casting |
Copper | 55 - 60 % Show Material materials with Copper of 55 - 60 % | ASTM B584 | Casting |
Iron | 1 - 3 % Show Material materials with Iron of 1 - 3 % | ASTM B584 | Casting |
Lead | 0.5 - 1.5 % Show Material materials with Lead of 0.5 - 1.5 % | ASTM B584 | Casting |
Manganese | 1 - 3.5 % Show Material materials with Manganese of 1 - 3.5 % | ASTM B584 | Casting |
Nickel | 1 % Show Material materials with Nickel of 1 % | ASTM B584 | Casting |
Tin | 1.5 % Show Material materials with Tin of 1.5 % | ASTM B584 | Casting |
Zinc | 30 - 38 % Show Material materials with Zinc of 30 - 38 % | ASTM B584 | Casting |