Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 100 - 125 GPa Show Material materials with Elastic modulus of 100 - 125 GPa | Typical for Wrought Copper Brass |
Hardness, Rockwell B | 23.0 °C | 85 - 94 [-] Show Material materials with Hardness, Rockwell B of 85 - 94 [-] | |
Hardness, Rockwell Superficial 30-T | 23.0 °C | 71 - 78 [-] Show Material materials with Hardness, Rockwell Superficial 30-T of 71 - 78 [-] | |
Shear modulus | 23.0 °C | 40 GPa Show Material materials with Shear modulus of 40 GPa | Typical for Wrought Copper Brass |
Tensile strength | 23.0 °C | 650 - 705 MPa Show Material materials with Tensile strength of 650 - 705 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 - 2.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K | Typical for Wrought Copper Brass |
Melting point | 875 - 1075 °C Show Material materials with Melting point of 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 23.0 °C | 371 - 418 J/(kg·K) Show Material materials with Specific heat capacity of 371 - 418 J/(kg·K) | Typical for Wrought Copper Brass |
Thermal conductivity | 23.0 °C | 100 - 234 W/(m·K) Show Material materials with Thermal conductivity of 100 - 234 W/(m·K) | Typical for Wrought Copper Brass |
Chemical properties
Property | Value |
---|---|
Copper | 94.5 - 96.5 % Show Material materials with Copper of 94.5 - 96.5 % |
Iron | 0.08 - 0.12 % Show Material materials with Iron of 0.08 - 0.12 % |
Lead | 0.05 % Show Material materials with Lead of 0.05 % |
Nickel | 0.11 - 0.2 % Show Material materials with Nickel of 0.11 - 0.2 % |
Phosphorus | 0.03 - 0.04 % Show Material materials with Phosphorus of 0.03 - 0.04 % |
Tin | 1.8 - 2.2 % Show Material materials with Tin of 1.8 - 2.2 % |