Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa | Typical for Wrought Copper High Copper Alloy |
Elongation A50 | 23.0 °C | 10 % Show Material materials with Elongation A50 of 10 % | |
Hardness, Rockwell B | 23.0 °C | 99 - 106 [-] Show Material materials with Hardness, Rockwell B of 99 - 106 [-] | |
Hardness, Rockwell Superficial 30-T | 23.0 °C | 82 - 89 [-] Show Material materials with Hardness, Rockwell Superficial 30-T of 82 - 89 [-] | |
Tensile strength | 23.0 °C | 825 - 965 MPa Show Material materials with Tensile strength of 825 - 965 MPa | |
Yield strength Rp0.2 | 23.0 °C | 720 - 860 MPa Show Material materials with Yield strength Rp0.2 of 720 - 860 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K | Typical for Wrought Copper High Copper Alloy |
Melting point | 855 - 1090 °C Show Material materials with Melting point of 855 - 1090 °C | Typical for Wrought Copper High Copper Alloy | |
Specific heat capacity | 23.0 °C | 360 - 420 J/(kg·K) Show Material materials with Specific heat capacity of 360 - 420 J/(kg·K) | Typical for Wrought Copper High Copper Alloy |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.2 % Show Material materials with Aluminium of 0.2 % |
Beryllium | 0.15 - 0.5 % Show Material materials with Beryllium of 0.15 - 0.5 % |
Iron | 0.2 % Show Material materials with Iron of 0.2 % |
Nickel | 1 - 1.4 % Show Material materials with Nickel of 1 - 1.4 % |
Silicon | 0.2 % Show Material materials with Silicon of 0.2 % |
Tin | 0.25 % Show Material materials with Tin of 0.25 % |
Zirconium | 0.5 % Show Material materials with Zirconium of 0.5 % |