EN 1652 Grade CuZn0.5 R220

Want to keep this datasheet? Save it now in your required format

Description

CuZn0,5, mat. No CW119C, is counted among unhardenable, low alloyed copper alloys. To the comparable make CuZn0,5, mat. No 2.0205, acc. to DIN 17666 : 1983-12 applies: A strength increase is achievable only by cold forming. According to the deformation level the tensile strength is between 220 and 360 N/mm². Temperature for removal of workhardening is above 250°C. Electrical conductivity is very high. Corrosion resistance is equal to unalloyed copper. Processing properties: hot forming: good cold forming: very good machinability: moderately soft and hard soldering: very good gas shielded welding: very good burnishing: good Application: For strips, construction parts and all types of hollow-ware as well as for heat transmission elements. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.9 - 8.92 g/cm³

Show Material materials with Density of 8.9 - 8.92 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

127 GPa

Show Material materials with Elastic modulus of 127 GPa

Elongation

20.0 °C

42 %

Show Material materials with Elongation of 42 %

Elongation A50

20.0 °C

33 %

Show Material materials with Elongation A50 of 33 %

Poisson's ratio

20.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Shear modulus

23.0 °C

48 GPa

Show Material materials with Shear modulus of 48 GPa

Typical for Wrought Copper Pure / Low Alloyed Copper

Tensile strength

20.0 °C

220 - 260 MPa

Show Material materials with Tensile strength of 220 - 260 MPa

Yield strength Rp0.2

20.0 °C

140 MPa

Show Material materials with Yield strength Rp0.2 of 140 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

300.0 °C

1.77E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.77E-5 1/K

Melting point

965 - 1100 °C

Show Material materials with Melting point of 965 - 1100 °C

Typical for Wrought Copper Pure / Low Alloyed Copper

Specific heat capacity

20.0 °C

386 J/(kg·K)

Show Material materials with Specific heat capacity of 386 J/(kg·K)

100.0 °C

395 J/(kg·K)

Show Material materials with Specific heat capacity of 395 J/(kg·K)

200.0 °C

407 J/(kg·K)

Show Material materials with Specific heat capacity of 407 J/(kg·K)

Thermal conductivity

20.0 °C

350 W/(m·K)

Show Material materials with Thermal conductivity of 350 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

4.80E+7 S/m

Show Material materials with Electrical conductivity of 4.80E+7 S/m

Specific Electrical conductivity

83 % IACS

Show Material materials with Specific Electrical conductivity of 83 % IACS

Chemical properties

PropertyValue

Phosphorus

0.02 %

Show Material materials with Phosphorus of 0.02 %

Zinc

0.1 - 1 %

Show Material materials with Zinc of 0.1 - 1 %