EN 1652 Grade CuZn10 R240

View suppliers (16)
Want to keep this datasheet? Save it now in your required format

Description

CuZn10 (CW501L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal conductivity is lower than for CuZn5. Favorable electrical conductivity. Corrosion resistance is similar to pure copper. Processing properties: warm forming: moderately cold forming: good machinability: unfavorable hard and soft soldering: very good TIG-welding: good burnishing: good CuZn10 is used in electrical engineering, for metal goods as well as in jewelry and watches industry, for projectile casings and as cladding and enamelling material. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.79 - 8.8 g/cm³

Show Material materials with Density of 8.79 - 8.8 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

20.0 °C

124 GPa

Show Material materials with Elastic modulus of 124 GPa

100.0 °C

123 GPa

Show Material materials with Elastic modulus of 123 GPa

200.0 °C

118 GPa

Show Material materials with Elastic modulus of 118 GPa

300.0 °C

113 GPa

Show Material materials with Elastic modulus of 113 GPa

400.0 °C

107 GPa

Show Material materials with Elastic modulus of 107 GPa

500.0 °C

98 GPa

Show Material materials with Elastic modulus of 98 GPa

600.0 °C

88 GPa

Show Material materials with Elastic modulus of 88 GPa

700.0 °C

78 GPa

Show Material materials with Elastic modulus of 78 GPa

Elongation

20.0 °C

45 - 47 %

Show Material materials with Elongation of 45 - 47 %

Elongation A100

20.0 °C

43 %

Show Material materials with Elongation A100 of 43 %

Elongation A11.3

20.0 °C

45 %

Show Material materials with Elongation A11.3 of 45 %

Elongation A50

20.0 °C

36 %

Show Material materials with Elongation A50 of 36 %

Poisson's ratio

20.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Shear modulus

20.0 °C

46 GPa

Show Material materials with Shear modulus of 46 GPa

Tensile strength

20.0 °C

240 - 290 MPa

Show Material materials with Tensile strength of 240 - 290 MPa

Yield strength Rp0.2

20.0 °C

140 - 150 MPa

Show Material materials with Yield strength Rp0.2 of 140 - 150 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

200.0 °C

1.9E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.9E-5 1/K

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

376 - 377 J/(kg·K)

Show Material materials with Specific heat capacity of 376 - 377 J/(kg·K)

100.0 °C

398 J/(kg·K)

Show Material materials with Specific heat capacity of 398 J/(kg·K)

200.0 °C

410 J/(kg·K)

Show Material materials with Specific heat capacity of 410 J/(kg·K)

300.0 °C

419 J/(kg·K)

Show Material materials with Specific heat capacity of 419 J/(kg·K)

400.0 °C

431 J/(kg·K)

Show Material materials with Specific heat capacity of 431 J/(kg·K)

500.0 °C

444 J/(kg·K)

Show Material materials with Specific heat capacity of 444 J/(kg·K)

600.0 °C

452 J/(kg·K)

Show Material materials with Specific heat capacity of 452 J/(kg·K)

700.0 °C

465 J/(kg·K)

Show Material materials with Specific heat capacity of 465 J/(kg·K)

Unlock all property charts

Thermal conductivity

20.0 °C

184 W/(m·K)

Show Material materials with Thermal conductivity of 184 W/(m·K)

80.0 °C

197 W/(m·K)

Show Material materials with Thermal conductivity of 197 W/(m·K)

120.0 °C

209 W/(m·K)

Show Material materials with Thermal conductivity of 209 W/(m·K)

160.0 °C

218 W/(m·K)

Show Material materials with Thermal conductivity of 218 W/(m·K)

200.0 °C

226 W/(m·K)

Show Material materials with Thermal conductivity of 226 W/(m·K)

Unlock all property charts

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

2.47E+7 - 2.50E+7 S/m

Show Material materials with Electrical conductivity of 2.47E+7 - 2.50E+7 S/m

Electrical resistivity

20.0 °C

4.1E-8 Ω·m

Show Material materials with Electrical resistivity of 4.1E-8 Ω·m

Specific Electrical conductivity

43 % IACS

Show Material materials with Specific Electrical conductivity of 43 % IACS

Chemical properties

PropertyValue

Aluminium

0.02 %

Show Material materials with Aluminium of 0.02 %

Copper

89 - 91 %

Show Material materials with Copper of 89 - 91 %

Iron

0.05 %

Show Material materials with Iron of 0.05 %

Lead

0.05 %

Show Material materials with Lead of 0.05 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Phosphorus

0.2 %

Show Material materials with Phosphorus of 0.2 %

Tin

0.1 %

Show Material materials with Tin of 0.1 %