Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.73 - 8.8 g/cm³ Show Material materials with Density of 8.73 - 8.8 g/cm³ |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 20.0 °C | 120 - 122 GPa Show Material materials with Elastic modulus of 120 - 122 GPa |
100.0 °C | 119 GPa Show Material materials with Elastic modulus of 119 GPa | |
200.0 °C | 114 GPa Show Material materials with Elastic modulus of 114 GPa | |
300.0 °C | 109 GPa Show Material materials with Elastic modulus of 109 GPa | |
400.0 °C | 103 GPa Show Material materials with Elastic modulus of 103 GPa | |
500.0 °C | 94 GPa Show Material materials with Elastic modulus of 94 GPa | |
600.0 °C | 84 GPa Show Material materials with Elastic modulus of 84 GPa | |
700.0 °C | 74 GPa Show Material materials with Elastic modulus of 74 GPa | |
Elongation A50 | 20.0 °C | 3 - 4 % Show Material materials with Elongation A50 of 3 - 4 % |
Poisson's ratio | 20.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] |
Shear modulus | 20.0 °C | 45 GPa Show Material materials with Shear modulus of 45 GPa |
Tensile strength | 20.0 °C | 410 - 490 MPa Show Material materials with Tensile strength of 410 - 490 MPa |
Yield strength Rp0.2 | 20.0 °C | 360 MPa Show Material materials with Yield strength Rp0.2 of 360 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 - 2.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K | Typical for Wrought Copper Brass |
Melting point | 875 - 1075 °C Show Material materials with Melting point of 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 - 380 J/(kg·K) Show Material materials with Specific heat capacity of 377 - 380 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 159 W/(m·K) Show Material materials with Thermal conductivity of 159 W/(m·K) | |
80.0 °C | 167 W/(m·K) Show Material materials with Thermal conductivity of 167 W/(m·K) | ||
120.0 °C | 172 W/(m·K) Show Material materials with Thermal conductivity of 172 W/(m·K) | ||
160.0 °C | 176 W/(m·K) Show Material materials with Thermal conductivity of 176 W/(m·K) | ||
200.0 °C | 184 W/(m·K) Show Material materials with Thermal conductivity of 184 W/(m·K) | ||
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 2.10E+7 - 2.20E+7 S/m Show Material materials with Electrical conductivity of 2.10E+7 - 2.20E+7 S/m |
Electrical resistivity | 20.0 °C | 4.7E-8 Ω·m Show Material materials with Electrical resistivity of 4.7E-8 Ω·m |
Specific Electrical conductivity | 36 - 38 % IACS Show Material materials with Specific Electrical conductivity of 36 - 38 % IACS |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.02 % Show Material materials with Aluminium of 0.02 % |
Copper | 84 - 86 % Show Material materials with Copper of 84 - 86 % |
Iron | 0.05 % Show Material materials with Iron of 0.05 % |
Lead | 0.05 % Show Material materials with Lead of 0.05 % |
Nickel | 0.3 % Show Material materials with Nickel of 0.3 % |
Phosphorus | 0.2 % Show Material materials with Phosphorus of 0.2 % |
Tin | 0.1 % Show Material materials with Tin of 0.1 % |