EN 1652 Grade CuZn20 H155

Want to keep this datasheet? Save it now in your required format

Description

CuZn20 (CW503L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are worse than for CuZn15. Corrosion resistance is similar to pure copper. Processing properties: warm forming: moderately cold forming: good machinability: moderately hard and soft soldering: very good TIG-welding: good burnishing: very good CuZn20 is used for metal goods, in jewelry industry and automotive electrics as well as for metall hoses and manometer. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.67 - 8.7 g/cm³

Show Material materials with Density of 8.67 - 8.7 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

20.0 °C

119 GPa

Show Material materials with Elastic modulus of 119 GPa

100.0 °C

116 GPa

Show Material materials with Elastic modulus of 116 GPa

200.0 °C

111 GPa

Show Material materials with Elastic modulus of 111 GPa

300.0 °C

106 GPa

Show Material materials with Elastic modulus of 106 GPa

400.0 °C

100 GPa

Show Material materials with Elastic modulus of 100 GPa

500.0 °C

91 GPa

Show Material materials with Elastic modulus of 91 GPa

600.0 °C

81 GPa

Show Material materials with Elastic modulus of 81 GPa

700.0 °C

71 GPa

Show Material materials with Elastic modulus of 71 GPa

Hardness, Vickers

20.0 °C

155 [-]

Show Material materials with Hardness, Vickers of 155 [-]

Poisson's ratio

20.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Shear modulus

20.0 °C

44 GPa

Show Material materials with Shear modulus of 44 GPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.7E-5 - 2.1E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K

Typical for Wrought Copper Brass

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 - 380 J/(kg·K)

Show Material materials with Specific heat capacity of 377 - 380 J/(kg·K)

100.0 °C

398 J/(kg·K)

Show Material materials with Specific heat capacity of 398 J/(kg·K)

200.0 °C

410 J/(kg·K)

Show Material materials with Specific heat capacity of 410 J/(kg·K)

300.0 °C

419 J/(kg·K)

Show Material materials with Specific heat capacity of 419 J/(kg·K)

400.0 °C

431 J/(kg·K)

Show Material materials with Specific heat capacity of 431 J/(kg·K)

Unlock all property charts

Thermal conductivity

20.0 °C

142 W/(m·K)

Show Material materials with Thermal conductivity of 142 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.90E+7 S/m

Show Material materials with Electrical conductivity of 1.90E+7 S/m

Electrical resistivity

20.0 °C

5.3E-8 Ω·m

Show Material materials with Electrical resistivity of 5.3E-8 Ω·m

Specific Electrical conductivity

33 % IACS

Show Material materials with Specific Electrical conductivity of 33 % IACS

Chemical properties

PropertyValue

Aluminium

0.02 %

Show Material materials with Aluminium of 0.02 %

Copper

79 - 81 %

Show Material materials with Copper of 79 - 81 %

Iron

0.05 %

Show Material materials with Iron of 0.05 %

Lead

0.05 %

Show Material materials with Lead of 0.05 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Phosphorus

0.2 %

Show Material materials with Phosphorus of 0.2 %

Tin

0.1 %

Show Material materials with Tin of 0.1 %