EN 1652 Grade CuZn30 R410

Want to keep this datasheet? Save it now in your required format

Description

CuZn30 (CW505L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn28. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very good machinability: moderately hard and soft soldering: very good TIG-welding: good burnishing: very good CuZn30 is used for deep drawing components, musical instruments, hose tubes, springing elements, clockfaces and as cladding material. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.5 - 8.55 g/cm³

Show Material materials with Density of 8.5 - 8.55 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

114 - 115 GPa

Show Material materials with Elastic modulus of 114 - 115 GPa

100.0 °C

112 GPa

Show Material materials with Elastic modulus of 112 GPa

200.0 °C

107 GPa

Show Material materials with Elastic modulus of 107 GPa

300.0 °C

103 GPa

Show Material materials with Elastic modulus of 103 GPa

400.0 °C

96 GPa

Show Material materials with Elastic modulus of 96 GPa

500.0 °C

88 GPa

Show Material materials with Elastic modulus of 88 GPa

600.0 °C

77 GPa

Show Material materials with Elastic modulus of 77 GPa

700.0 °C

67 GPa

Show Material materials with Elastic modulus of 67 GPa

Elongation

20.0 °C

15 %

Show Material materials with Elongation of 15 %

Elongation A50

20.0 °C

9 - 12 %

Show Material materials with Elongation A50 of 9 - 12 %

Poisson's ratio

20.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Shear modulus

23.0 °C

40 GPa

Show Material materials with Shear modulus of 40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

410 - 490 MPa

Show Material materials with Tensile strength of 410 - 490 MPa

Yield strength Rp0.2

20.0 °C

260 MPa

Show Material materials with Yield strength Rp0.2 of 260 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.9E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.9E-5 1/K

150.0 °C

1.9E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.9E-5 1/K

300.0 °C

2E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2E-5 1/K

Unlock all property charts

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Show Material materials with Specific heat capacity of 377 J/(kg·K)

100.0 °C

398 J/(kg·K)

Show Material materials with Specific heat capacity of 398 J/(kg·K)

200.0 °C

410 J/(kg·K)

Show Material materials with Specific heat capacity of 410 J/(kg·K)

300.0 °C

419 J/(kg·K)

Show Material materials with Specific heat capacity of 419 J/(kg·K)

400.0 °C

431 J/(kg·K)

Show Material materials with Specific heat capacity of 431 J/(kg·K)

500.0 °C

444 J/(kg·K)

Show Material materials with Specific heat capacity of 444 J/(kg·K)

600.0 °C

452 J/(kg·K)

Show Material materials with Specific heat capacity of 452 J/(kg·K)

700.0 °C

456 J/(kg·K)

Show Material materials with Specific heat capacity of 456 J/(kg·K)

Unlock all property charts

Thermal conductivity

-200.0 °C

50 W/(m·K)

Show Material materials with Thermal conductivity of 50 W/(m·K)

20.0 °C

121 - 126 W/(m·K)

Show Material materials with Thermal conductivity of 121 - 126 W/(m·K)

200.0 °C

147 W/(m·K)

Show Material materials with Thermal conductivity of 147 W/(m·K)

Unlock all property charts

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.60E+7 - 1.70E+7 S/m

Show Material materials with Electrical conductivity of 1.60E+7 - 1.70E+7 S/m

Electrical resistivity

200.0 °C

7.7E-8 Ω·m

Show Material materials with Electrical resistivity of 7.7E-8 Ω·m

500.0 °C

1.08E-7 Ω·m

Show Material materials with Electrical resistivity of 1.08E-7 Ω·m

Unlock all property charts

Specific Electrical conductivity

28 - 29 % IACS

Show Material materials with Specific Electrical conductivity of 28 - 29 % IACS

Chemical properties

PropertyValue

Aluminium

0.02 %

Show Material materials with Aluminium of 0.02 %

Copper

69 - 71 %

Show Material materials with Copper of 69 - 71 %

Iron

0.05 %

Show Material materials with Iron of 0.05 %

Lead

0.05 %

Show Material materials with Lead of 0.05 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Tin

0.1 %

Show Material materials with Tin of 0.1 %