EN 1652 Grade CuZn37 R550

View suppliers (36)
Want to keep this datasheet? Save it now in your required format

Description

CuZn37 (CW508L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn36. CuZn37 is the main alloy for cold forming. It shows favorable corrosion resistance to fresh water. Processing properties: warm forming: good cold forming: very good machinability: moderately hard soldering: good soft soldering: very good TIG-welding: moderately burnishing: very good CuZn37 is used for bulb bases, wire clamps for aerial lines, contact springs, metal and wooden screws, print roller and zip fastener. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.4 - 8.44 g/cm³

Show Material materials with Density of 8.4 - 8.44 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

110 GPa

Show Material materials with Elastic modulus of 110 GPa

100.0 °C

106 GPa

Show Material materials with Elastic modulus of 106 GPa

200.0 °C

102 GPa

Show Material materials with Elastic modulus of 102 GPa

300.0 °C

97 GPa

Show Material materials with Elastic modulus of 97 GPa

400.0 °C

89 GPa

Show Material materials with Elastic modulus of 89 GPa

500.0 °C

79 GPa

Show Material materials with Elastic modulus of 79 GPa

Elongation A100

20.0 °C

2 %

Show Material materials with Elongation A100 of 2 %

Elongation A11.3

20.0 °C

5 %

Show Material materials with Elongation A11.3 of 5 %

Shear modulus

23.0 °C

40 GPa

Show Material materials with Shear modulus of 40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

550 MPa

Show Material materials with Tensile strength of 550 MPa

Yield strength Rp0.2

20.0 °C

450 - 500 MPa

Show Material materials with Yield strength Rp0.2 of 450 - 500 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

150.0 °C

1.9E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.9E-5 1/K

300.0 °C

2.1E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.1E-5 1/K

650.0 °C

2.3E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.3E-5 1/K

800.0 °C

2.4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.4E-5 1/K

Unlock all property charts

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Show Material materials with Specific heat capacity of 377 J/(kg·K)

Thermal conductivity

-200.0 °C

50 W/(m·K)

Show Material materials with Thermal conductivity of 50 W/(m·K)

20.0 °C

120 W/(m·K)

Show Material materials with Thermal conductivity of 120 W/(m·K)

200.0 °C

142 W/(m·K)

Show Material materials with Thermal conductivity of 142 W/(m·K)

Unlock all property charts

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.50E+7 S/m

Show Material materials with Electrical conductivity of 1.50E+7 S/m

200.0 °C

1.20E+7 S/m

Show Material materials with Electrical conductivity of 1.20E+7 S/m

Unlock all property charts

Electrical resistivity

20.0 °C

6.6E-8 Ω·m

Show Material materials with Electrical resistivity of 6.6E-8 Ω·m

200.0 °C

8.3E-8 Ω·m

Show Material materials with Electrical resistivity of 8.3E-8 Ω·m

Unlock all property charts

Chemical properties

PropertyValue

Aluminium

0.02 - 0.05 %

Show Material materials with Aluminium of 0.02 - 0.05 %

Copper

62 - 64 %

Show Material materials with Copper of 62 - 64 %

Iron

0.1 %

Show Material materials with Iron of 0.1 %

Lead

0.1 %

Show Material materials with Lead of 0.1 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Phosphorus

0.2 %

Show Material materials with Phosphorus of 0.2 %

Tin

0.1 %

Show Material materials with Tin of 0.1 %