EN 1652 Grade CuZn37Pb0.5 H140

View suppliers (2)
Want to keep this datasheet? Save it now in your required format


Material CuZn37Pb0,5, mat. No. CW604N, is an unhardenable wrought alloy. To the comparable make CuZn37Pb0,5, mat. No. 2.0332 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded brass grade of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: good cold forming: good machinability: good hard soldering: moderately soft soldering: very good TIG-welding: moderately burnishing: very good Application: for extruded profiles of high accuracy, for circuit boards and wheels for watch industry as well as for pressure brass components.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.





20.0 °C

8.44 g/cm³

Show Material materials with Density of 8.44 g/cm³



Elastic modulus

20.0 °C

110 GPa

Show Material materials with Elastic modulus of 110 GPa

Hardness, Vickers

20.0 °C

140 - 170 [-]

Show Material materials with Hardness, Vickers of 140 - 170 [-]

Shear modulus

20.0 °C

38 GPa

Show Material materials with Shear modulus of 38 GPa



Coefficient of thermal expansion

200.0 °C

2.04E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.04E-5 1/K

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

23.0 °C

371 - 418 J/(kg·K)

Show Material materials with Specific heat capacity of 371 - 418 J/(kg·K)

Typical for Wrought Copper Brass

Thermal conductivity

20.0 °C

113 W/(m·K)

Show Material materials with Thermal conductivity of 113 W/(m·K)



Electrical conductivity

20.0 °C

1.47E+7 S/m

Show Material materials with Electrical conductivity of 1.47E+7 S/m

Electrical resistivity

20.0 °C

6.8E-8 Ω·m

Show Material materials with Electrical resistivity of 6.8E-8 Ω·m

Specific Electrical conductivity

25 % IACS

Show Material materials with Specific Electrical conductivity of 25 % IACS

Chemical properties



0.05 %

Show Material materials with Aluminium of 0.05 %


62 - 64 %

Show Material materials with Copper of 62 - 64 %


0.1 %

Show Material materials with Iron of 0.1 %


0.1 - 0.8 %

Show Material materials with Lead of 0.1 - 0.8 %


0.3 %

Show Material materials with Nickel of 0.3 %


0.2 %

Show Material materials with Tin of 0.2 %