EN 1652 Grade CuZn39Pb0.5 H165

View suppliers (3)
Want to keep this datasheet? Save it now in your required format

Description

Material CuZn39Pb0,5, mat. No. CW610N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb0,5, mat. No. 2.0372 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded brass grade of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: moderately machinability: good hard soldering: moderately soft soldering: very good TIG-welding: moderately burnishing: very good Application: For plug pins, fitting parts, rivets, condenser plates, floor plate screeding and drawing instruments.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.4 g/cm³

Show Material materials with Density of 8.4 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

20.0 °C

102 GPa

Show Material materials with Elastic modulus of 102 GPa

Hardness, Vickers

20.0 °C

165 [-]

Show Material materials with Hardness, Vickers of 165 [-]

Shear modulus

20.0 °C

37 GPa

Show Material materials with Shear modulus of 37 GPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

200.0 °C

2.04E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.04E-5 1/K

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

23.0 °C

371 - 418 J/(kg·K)

Show Material materials with Specific heat capacity of 371 - 418 J/(kg·K)

Typical for Wrought Copper Brass

Thermal conductivity

20.0 °C

109 W/(m·K)

Show Material materials with Thermal conductivity of 109 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.39E+7 S/m

Show Material materials with Electrical conductivity of 1.39E+7 S/m

Electrical resistivity

20.0 °C

7.2E-8 Ω·m

Show Material materials with Electrical resistivity of 7.2E-8 Ω·m

Chemical properties

PropertyValue

Aluminium

0.05 %

Show Material materials with Aluminium of 0.05 %

Copper

59 - 60.5 %

Show Material materials with Copper of 59 - 60.5 %

Iron

0.2 %

Show Material materials with Iron of 0.2 %

Lead

0.2 - 0.8 %

Show Material materials with Lead of 0.2 - 0.8 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Tin

0.2 %

Show Material materials with Tin of 0.2 %