General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.9 - 8.94 g/cm³ Show Material materials with Density of 8.9 - 8.94 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 129 - 132 GPa Show Material materials with Elastic modulus of 129 - 132 GPa | |
Elongation | 20.0 °C | 33 - 42 % Show Material materials with Elongation of 33 - 42 % | |
Hardness, Vickers | 20.0 °C | 55 [-] Show Material materials with Hardness, Vickers of 55 [-] | |
Poisson's ratio | 20.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Shear modulus | 23.0 °C | 48 GPa Show Material materials with Shear modulus of 48 GPa | Typical for Wrought Copper Pure / Low Alloyed Copper |
Tensile strength | 20.0 °C | 200 - 250 MPa Show Material materials with Tensile strength of 200 - 250 MPa | |
Yield strength Rp0.2 | 20.0 °C | 40 - 100 MPa Show Material materials with Yield strength Rp0.2 of 40 - 100 MPa | |
Yield strength Rp1.0 | 50.0 °C | 60 MPa Show Material materials with Yield strength Rp1.0 of 60 MPa | |
100.0 °C | 55 MPa Show Material materials with Yield strength Rp1.0 of 55 MPa | ||
150.0 °C | 55 MPa Show Material materials with Yield strength Rp1.0 of 55 MPa | ||
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K | Typical for Wrought Copper Pure / Low Alloyed Copper |
Melting point | 965 - 1100 °C Show Material materials with Melting point of 965 - 1100 °C | Typical for Wrought Copper Pure / Low Alloyed Copper | |
Specific heat capacity | 20.0 °C | 385 - 386 J/(kg·K) Show Material materials with Specific heat capacity of 385 - 386 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 350 - 352 W/(m·K) Show Material materials with Thermal conductivity of 350 - 352 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 5.20E+7 S/m Show Material materials with Electrical conductivity of 5.20E+7 S/m |
Electrical resistivity | 20.0 °C | 1.9E-8 Ω·m Show Material materials with Electrical resistivity of 1.9E-8 Ω·m |
Chemical properties