General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.3 - 8.8 g/cm³ Show Material materials with Density of 8.3 - 8.8 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa | Typical for Wrought Copper High Copper Alloy |
Elongation | 20.0 °C | 8 - 12 % Show Material materials with Elongation of 8 - 12 % | |
Elongation A10 | 20.0 °C | 8 % Show Material materials with Elongation A10 of 8 % | |
Elongation A100 | 20.0 °C | 6 % Show Material materials with Elongation A100 of 6 % | |
Hardness, Brinell | 20.0 °C | 90 - 320 [-] Show Material materials with Hardness, Brinell of 90 - 320 [-] | |
Hardness, Vickers | 20.0 °C | 200 - 230 [-] Show Material materials with Hardness, Vickers of 200 - 230 [-] | |
Tensile strength | 20.0 °C | 650 - 900 MPa Show Material materials with Tensile strength of 650 - 900 MPa | |
Yield strength Rp0.2 | 20.0 °C | 500 - 635 MPa Show Material materials with Yield strength Rp0.2 of 500 - 635 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K | Typical for Wrought Copper High Copper Alloy |
Melting point | 855 - 1090 °C Show Material materials with Melting point of 855 - 1090 °C | Typical for Wrought Copper High Copper Alloy | |
Specific heat capacity | 23.0 °C | 360 - 420 J/(kg·K) Show Material materials with Specific heat capacity of 360 - 420 J/(kg·K) | Typical for Wrought Copper High Copper Alloy |
Chemical properties
Property | Value |
---|---|
Beryllium | 0.4 - 0.7 % Show Material materials with Beryllium of 0.4 - 0.7 % |
Cobalt | 0.8 - 1.3 % Show Material materials with Cobalt of 0.8 - 1.3 % |
Iron | 0.2 % Show Material materials with Iron of 0.2 % |
Nickel | 0.8 - 1.3 % Show Material materials with Nickel of 0.8 - 1.3 % |