General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.92 g/cm³ Show Material materials with Density of 8.92 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa | Typical for Wrought Copper High Copper Alloy |
Elongation | 20.0 °C | 25 % Show Material materials with Elongation of 25 % | |
Elongation A10 | 20.0 °C | 22 % Show Material materials with Elongation A10 of 22 % | |
Elongation A100 | 20.0 °C | 20 % Show Material materials with Elongation A100 of 20 % | |
Hardness, Brinell | 20.0 °C | 65 - 95 [-] Show Material materials with Hardness, Brinell of 65 - 95 [-] | |
Hardness, Vickers | 20.0 °C | 70 - 100 [-] Show Material materials with Hardness, Vickers of 70 - 100 [-] | |
Tensile strength | 20.0 °C | 250 MPa Show Material materials with Tensile strength of 250 MPa | |
Yield strength Rp0.2 | 20.0 °C | 140 MPa Show Material materials with Yield strength Rp0.2 of 140 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 300.0 °C | 1.77E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.77E-5 1/K | |
Melting point | 855 - 1090 °C Show Material materials with Melting point of 855 - 1090 °C | Typical for Wrought Copper High Copper Alloy | |
Specific heat capacity | 20.0 °C | 385 J/(kg·K) Show Material materials with Specific heat capacity of 385 J/(kg·K) |
Chemical properties
Property | Value |
---|---|
Nickel | 0.8 - 1.2 % Show Material materials with Nickel of 0.8 - 1.2 % |
Phosphorus | 0.15 - 0.25 % Show Material materials with Phosphorus of 0.15 - 0.25 % |