EN 12163 Grade CuNi2Be F00

View suppliers (2)
Want to keep this datasheet? Save it now in your required format

Description

CuNi2Be, mat. No CW110C, is counted among hardenable, low alloyed copper alloys. To the comparable make CuNi2Be, mat. No 2.0850, acc. to DIN 17666 : 1983-12 applies: The alloy shows high tensile strength and high temperature resistance and mean electrical and favorable thermal conductivity. Processing properties: hot and cold forming: good machinability: moderately hard and soft soldering: good gas shielded welding: good burnishing: good Application: For resistance welding electrodes as well as for springs. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.8 g/cm³

Show Material materials with Density of 8.8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

110 - 130 GPa

Show Material materials with Elastic modulus of 110 - 130 GPa

Typical for Wrought Copper High Copper Alloy

Elongation

20.0 °C

10 - 12 %

Show Material materials with Elongation of 10 - 12 %

Elongation A10

20.0 °C

8 %

Show Material materials with Elongation A10 of 8 %

Elongation A100

20.0 °C

6 %

Show Material materials with Elongation A100 of 6 %

Hardness, Brinell

20.0 °C

190 - 220 [-]

Show Material materials with Hardness, Brinell of 190 - 220 [-]

Hardness, Vickers

20.0 °C

200 - 230 [-]

Show Material materials with Hardness, Vickers of 200 - 230 [-]

Tensile strength

20.0 °C

650 - 900 MPa

Show Material materials with Tensile strength of 650 - 900 MPa

Yield strength Rp0.2

20.0 °C

500 - 635 MPa

Show Material materials with Yield strength Rp0.2 of 500 - 635 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.6E-5 - 1.8E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K

Typical for Wrought Copper High Copper Alloy

Melting point

855 - 1090 °C

Show Material materials with Melting point of 855 - 1090 °C

Typical for Wrought Copper High Copper Alloy

Specific heat capacity

23.0 °C

360 - 420 J/(kg·K)

Show Material materials with Specific heat capacity of 360 - 420 J/(kg·K)

Typical for Wrought Copper High Copper Alloy

Chemical properties

PropertyValue

Beryllium

0.2 - 0.6 %

Show Material materials with Beryllium of 0.2 - 0.6 %

Cobalt

0.3 %

Show Material materials with Cobalt of 0.3 %

Iron

0.2 %

Show Material materials with Iron of 0.2 %

Nickel

1.4 - 2.4 %

Show Material materials with Nickel of 1.4 - 2.4 %