General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.9 g/cm³ Show Material materials with Density of 8.9 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa | Typical for Wrought Copper High Copper Alloy |
Elongation | 20.0 °C | 8 - 12 % Show Material materials with Elongation of 8 - 12 % | |
Elongation A10 | 20.0 °C | 7 - 9 % Show Material materials with Elongation A10 of 7 - 9 % | |
Hardness, Brinell | 20.0 °C | 120 - 180 [-] Show Material materials with Hardness, Brinell of 120 - 180 [-] | |
Hardness, Vickers | 20.0 °C | 125 - 185 [-] Show Material materials with Hardness, Vickers of 125 - 185 [-] | |
Tensile strength | 20.0 °C | 400 - 470 MPa Show Material materials with Tensile strength of 400 - 470 MPa | |
Yield strength Rp0.2 | 20.0 °C | 310 - 380 MPa Show Material materials with Yield strength Rp0.2 of 310 - 380 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K | Typical for Wrought Copper High Copper Alloy |
Melting point | 855 - 1090 °C Show Material materials with Melting point of 855 - 1090 °C | Typical for Wrought Copper High Copper Alloy | |
Specific heat capacity | 23.0 °C | 360 - 420 J/(kg·K) Show Material materials with Specific heat capacity of 360 - 420 J/(kg·K) | Typical for Wrought Copper High Copper Alloy |
Chemical properties
Property | Value |
---|---|
Chromium | 0.5 - 1.2 % Show Material materials with Chromium of 0.5 - 1.2 % |
Iron | 0.08 % Show Material materials with Iron of 0.08 % |
Silicon | 0.1 % Show Material materials with Silicon of 0.1 % |