EN 12163 Grade CuCr1 F00

Want to keep this datasheet? Save it now in your required format

Description

The material CuCr1 , mat. No CW105C is incomparable to a DIN-make. It is used in the form of bars, prematerial for forged parts, wires, profiles and forged parts.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

110 - 130 GPa

Show Material materials with Elastic modulus of 110 - 130 GPa

Typical for Wrought Copper High Copper Alloy

Hardness, Brinell

20.0 °C

105 [-]

Show Material materials with Hardness, Brinell of 105 [-]

Hardness, Vickers

20.0 °C

110 [-]

Show Material materials with Hardness, Vickers of 110 [-]

Tensile strength

20.0 °C

360 - 370 MPa

Show Material materials with Tensile strength of 360 - 370 MPa

Yield strength Rp0.2

20.0 °C

250 - 300 MPa

Show Material materials with Yield strength Rp0.2 of 250 - 300 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.6E-5 - 1.8E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K

Typical for Wrought Copper High Copper Alloy

Melting point

855 - 1090 °C

Show Material materials with Melting point of 855 - 1090 °C

Typical for Wrought Copper High Copper Alloy

Specific heat capacity

23.0 °C

360 - 420 J/(kg·K)

Show Material materials with Specific heat capacity of 360 - 420 J/(kg·K)

Typical for Wrought Copper High Copper Alloy

Chemical properties

PropertyValue

Chromium

0.5 - 1.2 %

Show Material materials with Chromium of 0.5 - 1.2 %

Iron

0.08 %

Show Material materials with Iron of 0.08 %

Silicon

0.1 %

Show Material materials with Silicon of 0.1 %