General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.8 - 8.9 g/cm³ Show Material materials with Density of 8.8 - 8.9 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa | Typical for Wrought Copper High Copper Alloy |
Elongation | 20.0 °C | 8 - 16 % Show Material materials with Elongation of 8 - 16 % | |
Elongation A10 | 20.0 °C | 6 - 10 % Show Material materials with Elongation A10 of 6 - 10 % | |
Elongation A100 | 20.0 °C | 5 - 8 % Show Material materials with Elongation A100 of 5 - 8 % | |
Hardness, Brinell | 20.0 °C | 85 - 170 [-] Show Material materials with Hardness, Brinell of 85 - 170 [-] | |
Hardness, Vickers | 20.0 °C | 90 - 180 [-] Show Material materials with Hardness, Vickers of 90 - 180 [-] | |
Tensile strength | 20.0 °C | 300 - 590 MPa Show Material materials with Tensile strength of 300 - 590 MPa | |
Yield strength Rp0.2 | 20.0 °C | 210 - 570 MPa Show Material materials with Yield strength Rp0.2 of 210 - 570 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 300.0 °C | 1.68E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.68E-5 1/K | |
Melting point | 855 - 1090 °C Show Material materials with Melting point of 855 - 1090 °C | Typical for Wrought Copper High Copper Alloy | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) Show Material materials with Specific heat capacity of 377 J/(kg·K) |
Chemical properties
Property | Value |
---|---|
Iron | 0.2 % Show Material materials with Iron of 0.2 % |
Lead | 0.02 % Show Material materials with Lead of 0.02 % |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % |
Nickel | 1 - 1.6 % Show Material materials with Nickel of 1 - 1.6 % |
Silicon | 0.4 - 0.7 % Show Material materials with Silicon of 0.4 - 0.7 % |