EN 12163 Grade CuZn33 M

Want to keep this datasheet? Save it now in your required format


CuZn33 (CW506L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn30. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very good machinability: moderately hard and soft soldering: very good TIG-welding: good burnishing: very good CuZn33 is used for deep drawing components, metal goods, watch parts, polishing sheet, wire mesh, cooler strips, tubular rivets and as etching brass. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.





20.0 °C

8.5 g/cm³

Show Material materials with Density of 8.5 g/cm³



Elastic modulus

20.0 °C

112 GPa

Show Material materials with Elastic modulus of 112 GPa

Poisson's ratio

20.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Shear modulus

20.0 °C

40 GPa

Show Material materials with Shear modulus of 40 GPa



Coefficient of thermal expansion

23.0 °C

1.7E-5 - 2.1E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K

Typical for Wrought Copper Brass

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Show Material materials with Specific heat capacity of 377 J/(kg·K)

Thermal conductivity

20.0 °C

121 W/(m·K)

Show Material materials with Thermal conductivity of 121 W/(m·K)



Electrical conductivity

20.0 °C

1.55E+7 - 1.60E+7 S/m

Show Material materials with Electrical conductivity of 1.55E+7 - 1.60E+7 S/m

Electrical resistivity

20.0 °C

6.5E-8 Ω·m

Show Material materials with Electrical resistivity of 6.5E-8 Ω·m

Specific Electrical conductivity

28 % IACS

Show Material materials with Specific Electrical conductivity of 28 % IACS

Chemical properties



0.02 %

Show Material materials with Aluminium of 0.02 %


66 - 68.5 %

Show Material materials with Copper of 66 - 68.5 %


0.05 %

Show Material materials with Iron of 0.05 %


0.05 %

Show Material materials with Lead of 0.05 %


0.3 %

Show Material materials with Nickel of 0.3 %


0.1 %

Show Material materials with Tin of 0.1 %