General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.4 - 8.47 g/cm³ Show Material materials with Density of 8.4 - 8.47 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | -195.0 °C | 108 GPa Show Material materials with Elastic modulus of 108 GPa | |
-100.0 °C | 106 GPa Show Material materials with Elastic modulus of 106 GPa | ||
20.0 °C | 96 - 105 GPa Show Material materials with Elastic modulus of 96 - 105 GPa | ||
50.0 °C | 100 GPa Show Material materials with Elastic modulus of 100 GPa | ||
100.0 °C | 93 GPa Show Material materials with Elastic modulus of 93 GPa | ||
150.0 °C | 91 GPa Show Material materials with Elastic modulus of 91 GPa | ||
200.0 °C | 89 GPa Show Material materials with Elastic modulus of 89 GPa | ||
250.0 °C | 83 GPa Show Material materials with Elastic modulus of 83 GPa | ||
Elongation | 20.0 °C | 20 % Show Material materials with Elongation of 20 % | |
Elongation A11.3 | 20.0 °C | 15 % Show Material materials with Elongation A11.3 of 15 % | |
Shear modulus | 23.0 °C | 40 GPa Show Material materials with Shear modulus of 40 GPa | Typical for Wrought Copper Brass |
Tensile strength | 20.0 °C | 340 - 360 MPa Show Material materials with Tensile strength of 340 - 360 MPa | |
Yield strength Rp0.2 | 20.0 °C | 120 - 320 MPa Show Material materials with Yield strength Rp0.2 of 120 - 320 MPa | |
Yield strength Rp1.0 | 20.0 °C | 140 MPa Show Material materials with Yield strength Rp1.0 of 140 MPa | |
50.0 °C | 140 MPa Show Material materials with Yield strength Rp1.0 of 140 MPa | ||
100.0 °C | 137 MPa Show Material materials with Yield strength Rp1.0 of 137 MPa | ||
150.0 °C | 137 MPa Show Material materials with Yield strength Rp1.0 of 137 MPa | ||
200.0 °C | 132 MPa Show Material materials with Yield strength Rp1.0 of 132 MPa | ||
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.93E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.93E-5 1/K | |
200.0 °C | 2.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.1E-5 1/K | ||
300.0 °C | 2.14E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.14E-5 1/K | ||
800.0 °C | 2.47E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.47E-5 1/K | ||
Melting point | 875 - 1075 °C Show Material materials with Melting point of 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) Show Material materials with Specific heat capacity of 377 J/(kg·K) | |
Thermal conductivity | -200.0 °C | 50 W/(m·K) Show Material materials with Thermal conductivity of 50 W/(m·K) | |
20.0 °C | 113 - 123 W/(m·K) Show Material materials with Thermal conductivity of 113 - 123 W/(m·K) | ||
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 1.46E+7 - 1.50E+7 S/m Show Material materials with Electrical conductivity of 1.46E+7 - 1.50E+7 S/m |
200.0 °C | 1.20E+7 S/m Show Material materials with Electrical conductivity of 1.20E+7 S/m | |
Electrical resistivity | 20.0 °C | 6.6E-8 Ω·m Show Material materials with Electrical resistivity of 6.6E-8 Ω·m |
200.0 °C | 8.3E-8 Ω·m Show Material materials with Electrical resistivity of 8.3E-8 Ω·m | |
Specific Electrical conductivity | 25 - 25.2 % IACS Show Material materials with Specific Electrical conductivity of 25 - 25.2 % IACS |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.05 % Show Material materials with Aluminium of 0.05 % |
Copper | 57 - 59 % Show Material materials with Copper of 57 - 59 % |
Iron | 0.3 % Show Material materials with Iron of 0.3 % |
Lead | 2.5 - 3.5 % Show Material materials with Lead of 2.5 - 3.5 % |
Nickel | 0.3 % Show Material materials with Nickel of 0.3 % |
Tin | 0.3 % Show Material materials with Tin of 0.3 % |