EN 12164 Grade CuZn40 R400

View suppliers (13)
Want to keep this datasheet? Save it now in your required format

Description

CuZn40 (CW509L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn37. Corrosion resistance is similar to pure copper. Processing properties: warm forming: very good cold forming: good machinability: moderately hard soldering: good soft soldering: very good TIG-welding: moderately burnishing: very good CuZn40 is used for hot-pressed forgings, metal fitting and lock components, for nipple wire, condenser bottoms and watchcases.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.4 - 8.41 g/cm³

Show Material materials with Density of 8.4 - 8.41 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-195.0 °C

108 GPa

Show Material materials with Elastic modulus of 108 GPa

-100.0 °C

106 GPa

Show Material materials with Elastic modulus of 106 GPa

20.0 °C

102 - 105 GPa

Show Material materials with Elastic modulus of 102 - 105 GPa

50.0 °C

100 GPa

Show Material materials with Elastic modulus of 100 GPa

100.0 °C

93 - 99 GPa

Show Material materials with Elastic modulus of 93 - 99 GPa

150.0 °C

91 GPa

Show Material materials with Elastic modulus of 91 GPa

200.0 °C

89 - 94 GPa

Show Material materials with Elastic modulus of 89 - 94 GPa

250.0 °C

83 GPa

Show Material materials with Elastic modulus of 83 GPa

300.0 °C

89 GPa

Show Material materials with Elastic modulus of 89 GPa

400.0 °C

83 GPa

Show Material materials with Elastic modulus of 83 GPa

500.0 °C

74 GPa

Show Material materials with Elastic modulus of 74 GPa

600.0 °C

64 GPa

Show Material materials with Elastic modulus of 64 GPa

700.0 °C

54 GPa

Show Material materials with Elastic modulus of 54 GPa

Elongation

20.0 °C

20 - 23 %

Show Material materials with Elongation of 20 - 23 %

Elongation A50

20.0 °C

15 %

Show Material materials with Elongation A50 of 15 %

Elongation, transverse

20.0 °C

23 %

Show Material materials with Elongation, transverse of 23 %

Poisson's ratio

20.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Shear modulus

20.0 °C

37 GPa

Show Material materials with Shear modulus of 37 GPa

Tensile strength

20.0 °C

400 - 480 MPa

Show Material materials with Tensile strength of 400 - 480 MPa

Tensile strength, transverse

20.0 °C

400 MPa

Show Material materials with Tensile strength, transverse of 400 MPa

Yield strength Rp0.2

20.0 °C

190 - 250 MPa

Show Material materials with Yield strength Rp0.2 of 190 - 250 MPa

50.0 °C

250 MPa

Show Material materials with Yield strength Rp0.2 of 250 MPa

100.0 °C

225 MPa

Show Material materials with Yield strength Rp0.2 of 225 MPa

150.0 °C

200 MPa

Show Material materials with Yield strength Rp0.2 of 200 MPa

Unlock all property charts

Yield strength Rp0.2, transverse

20.0 °C

240 MPa

Show Material materials with Yield strength Rp0.2, transverse of 240 MPa

50.0 °C

240 MPa

Show Material materials with Yield strength Rp0.2, transverse of 240 MPa

100.0 °C

220 MPa

Show Material materials with Yield strength Rp0.2, transverse of 220 MPa

150.0 °C

200 MPa

Show Material materials with Yield strength Rp0.2, transverse of 200 MPa

Unlock all property charts

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.7E-5 - 2.1E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K

Typical for Wrought Copper Brass

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

375 - 377 J/(kg·K)

Show Material materials with Specific heat capacity of 375 - 377 J/(kg·K)

Thermal conductivity

20.0 °C

109 - 117 W/(m·K)

Show Material materials with Thermal conductivity of 109 - 117 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.39E+7 - 1.50E+7 S/m

Show Material materials with Electrical conductivity of 1.39E+7 - 1.50E+7 S/m

Electrical resistivity

20.0 °C

6.7E-8 Ω·m

Show Material materials with Electrical resistivity of 6.7E-8 Ω·m

Specific Electrical conductivity

24 - 26 % IACS

Show Material materials with Specific Electrical conductivity of 24 - 26 % IACS

Chemical properties

PropertyValue

Aluminium

0.05 %

Show Material materials with Aluminium of 0.05 %

Copper

59 - 61.5 %

Show Material materials with Copper of 59 - 61.5 %

Iron

0.2 %

Show Material materials with Iron of 0.2 %

Lead

0.2 - 0.3 %

Show Material materials with Lead of 0.2 - 0.3 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Tin

0.2 %

Show Material materials with Tin of 0.2 %