EN 12165 Grade CuCo1Ni1Be TB00

Want to keep this datasheet? Save it now in your required format

Description

The material CuCo1Ni1Be , mat. No CW103C is incomparable to a DIN-make. It is used in the form of plates, sheets, stripes, circular blanks, bars, prematerial for forged parts, wires, profiles and forged parts.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value
Density	20.0 °C	8.3 - 8.8 g/cm³ Show Material materials with Density of 8.3 - 8.8 g/cm³

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa	Typical for Wrought Copper High Copper Alloy
Elongation	20.0 °C	20 - 25 % Show Material materials with Elongation of 20 - 25 %
Elongation A10	20.0 °C	18 - 22 % Show Material materials with Elongation A10 of 18 - 22 %
Elongation A100	20.0 °C	15 - 20 % Show Material materials with Elongation A100 of 15 - 20 %
Hardness, Brinell	20.0 °C	65 - 95 [-] Show Material materials with Hardness, Brinell of 65 - 95 [-]
Hardness, Vickers	20.0 °C	70 - 100 [-] Show Material materials with Hardness, Vickers of 70 - 100 [-]
Tensile strength	20.0 °C	240 - 380 MPa Show Material materials with Tensile strength of 240 - 380 MPa
Yield strength Rp0.2	20.0 °C	135 - 200 MPa Show Material materials with Yield strength Rp0.2 of 135 - 200 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1.6E-5 - 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K	Typical for Wrought Copper High Copper Alloy
Melting point		855 - 1090 °C Show Material materials with Melting point of 855 - 1090 °C	Typical for Wrought Copper High Copper Alloy
Specific heat capacity	23.0 °C	360 - 420 J/(kg·K) Show Material materials with Specific heat capacity of 360 - 420 J/(kg·K)	Typical for Wrought Copper High Copper Alloy

Chemical properties

Property	Value
Beryllium	0.4 - 0.7 % Show Material materials with Beryllium of 0.4 - 0.7 %
Cobalt	0.8 - 1.3 % Show Material materials with Cobalt of 0.8 - 1.3 %
Iron	0.2 % Show Material materials with Iron of 0.2 %
Nickel	0.8 - 1.3 % Show Material materials with Nickel of 0.8 - 1.3 %