EN 12166 Grade CuBe2Pb TH

Want to keep this datasheet? Save it now in your required format

Description

CuBe2Pb, mat. No CW102C, is counted among hardenable, low alloyed copper alloys. To the comparable make CuBe2Pb, mat. No 2.1248, acc. to DIN 17666 : 1983-12 applies: The alloy shows a very high tensile strength and increased temperature resistance and mean electrical and favorable thermal conductivity. Processing properties: hot and cold forming: good machinability: moderately hard and soft soldering: good gas shielded welding: good burnishing: good Application: For all types of springs, membranes, wear resistant parts, as well as for non-sparking tools.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

110 - 130 GPa

Show Material materials with Elastic modulus of 110 - 130 GPa

Typical for Wrought Copper High Copper Alloy

Elongation

20.0 °C

2 - 15 %

Show Material materials with Elongation of 2 - 15 %

Elongation A10

20.0 °C

8 %

Show Material materials with Elongation A10 of 8 %

Elongation A100

20.0 °C

6 - 10 %

Show Material materials with Elongation A100 of 6 - 10 %

Hardness, Vickers

20.0 °C

120 - 290 [-]

Show Material materials with Hardness, Vickers of 120 - 290 [-]

Tensile strength

20.0 °C

510 - 1140 MPa

Show Material materials with Tensile strength of 510 - 1140 MPa

Yield strength Rp0.2

20.0 °C

480 - 920 MPa

Show Material materials with Yield strength Rp0.2 of 480 - 920 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.6E-5 - 1.8E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K

Typical for Wrought Copper High Copper Alloy

Melting point

855 - 1090 °C

Show Material materials with Melting point of 855 - 1090 °C

Typical for Wrought Copper High Copper Alloy

Specific heat capacity

23.0 °C

360 - 420 J/(kg·K)

Show Material materials with Specific heat capacity of 360 - 420 J/(kg·K)

Typical for Wrought Copper High Copper Alloy

Chemical properties

PropertyValue

Beryllium

1.8 - 2 %

Show Material materials with Beryllium of 1.8 - 2 %

Cobalt

0.3 %

Show Material materials with Cobalt of 0.3 %

Iron

0.2 %

Show Material materials with Iron of 0.2 %

Lead

0.2 - 0.6 %

Show Material materials with Lead of 0.2 - 0.6 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %