EN 12166 Grade CuZn15 R300

View suppliers (17)
Want to keep this datasheet? Save it now in your required format

Description

CuZn15 (CW502L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn10. Corrosion resistance is similar to pure copper. Processing properties: warm forming: moderately cold forming: good machinability: moderately hard and soft soldering: very good TIG-welding: good burnishing: very good CuZn15 is used in electrical engineering, for metal goods as well as in jewelry industry, for metall hoses, pressure measuring instruments, signs, casings and suspension bodies. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.73 - 8.8 g/cm³

Show Material materials with Density of 8.73 - 8.8 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

20.0 °C

120 - 122 GPa

Show Material materials with Elastic modulus of 120 - 122 GPa

100.0 °C

119 GPa

Show Material materials with Elastic modulus of 119 GPa

200.0 °C

114 GPa

Show Material materials with Elastic modulus of 114 GPa

300.0 °C

109 GPa

Show Material materials with Elastic modulus of 109 GPa

400.0 °C

103 GPa

Show Material materials with Elastic modulus of 103 GPa

500.0 °C

94 GPa

Show Material materials with Elastic modulus of 94 GPa

600.0 °C

84 GPa

Show Material materials with Elastic modulus of 84 GPa

700.0 °C

74 GPa

Show Material materials with Elastic modulus of 74 GPa

Elongation

20.0 °C

25 %

Show Material materials with Elongation of 25 %

Elongation A50

20.0 °C

16 - 20 %

Show Material materials with Elongation A50 of 16 - 20 %

Poisson's ratio

20.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Shear modulus

20.0 °C

45 GPa

Show Material materials with Shear modulus of 45 GPa

Tensile strength

20.0 °C

300 - 370 MPa

Show Material materials with Tensile strength of 300 - 370 MPa

Yield strength Rp0.2

20.0 °C

150 MPa

Show Material materials with Yield strength Rp0.2 of 150 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.7E-5 - 2.1E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K

Typical for Wrought Copper Brass

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 - 380 J/(kg·K)

Show Material materials with Specific heat capacity of 377 - 380 J/(kg·K)

Thermal conductivity

20.0 °C

159 W/(m·K)

Show Material materials with Thermal conductivity of 159 W/(m·K)

80.0 °C

167 W/(m·K)

Show Material materials with Thermal conductivity of 167 W/(m·K)

120.0 °C

172 W/(m·K)

Show Material materials with Thermal conductivity of 172 W/(m·K)

160.0 °C

176 W/(m·K)

Show Material materials with Thermal conductivity of 176 W/(m·K)

200.0 °C

184 W/(m·K)

Show Material materials with Thermal conductivity of 184 W/(m·K)

Unlock all property charts

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

2.10E+7 - 2.20E+7 S/m

Show Material materials with Electrical conductivity of 2.10E+7 - 2.20E+7 S/m

Electrical resistivity

20.0 °C

4.7E-8 Ω·m

Show Material materials with Electrical resistivity of 4.7E-8 Ω·m

Specific Electrical conductivity

36 - 38 % IACS

Show Material materials with Specific Electrical conductivity of 36 - 38 % IACS

Chemical properties

PropertyValue

Aluminium

0.02 %

Show Material materials with Aluminium of 0.02 %

Copper

84 - 86 %

Show Material materials with Copper of 84 - 86 %

Iron

0.05 %

Show Material materials with Iron of 0.05 %

Lead

0.05 %

Show Material materials with Lead of 0.05 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Phosphorus

0.2 %

Show Material materials with Phosphorus of 0.2 %

Tin

0.1 %

Show Material materials with Tin of 0.1 %