Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.5 - 8.55 g/cm³ Show Material materials with Density of 8.5 - 8.55 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 114 - 115 GPa Show Material materials with Elastic modulus of 114 - 115 GPa | |
100.0 °C | 112 GPa Show Material materials with Elastic modulus of 112 GPa | ||
200.0 °C | 107 GPa Show Material materials with Elastic modulus of 107 GPa | ||
300.0 °C | 103 GPa Show Material materials with Elastic modulus of 103 GPa | ||
400.0 °C | 96 GPa Show Material materials with Elastic modulus of 96 GPa | ||
500.0 °C | 88 GPa Show Material materials with Elastic modulus of 88 GPa | ||
600.0 °C | 77 GPa Show Material materials with Elastic modulus of 77 GPa | ||
700.0 °C | 67 GPa Show Material materials with Elastic modulus of 67 GPa | ||
Elongation A100 | 20.0 °C | 3 % Show Material materials with Elongation A100 of 3 % | |
Elongation A50 | 20.0 °C | 2 % Show Material materials with Elongation A50 of 2 % | |
Poisson's ratio | 20.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Shear modulus | 23.0 °C | 40 GPa Show Material materials with Shear modulus of 40 GPa | Typical for Wrought Copper Brass |
Tensile strength | 20.0 °C | 550 - 640 MPa Show Material materials with Tensile strength of 550 - 640 MPa | |
Yield strength Rp0.2 | 20.0 °C | 450 MPa Show Material materials with Yield strength Rp0.2 of 450 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.9E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.9E-5 1/K | |
150.0 °C | 1.9E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.9E-5 1/K | ||
300.0 °C | 2E-5 1/K Show Material materials with Coefficient of thermal expansion of 2E-5 1/K | ||
Melting point | 875 - 1075 °C Show Material materials with Melting point of 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) Show Material materials with Specific heat capacity of 377 J/(kg·K) | |
100.0 °C | 398 J/(kg·K) Show Material materials with Specific heat capacity of 398 J/(kg·K) | ||
200.0 °C | 410 J/(kg·K) Show Material materials with Specific heat capacity of 410 J/(kg·K) | ||
300.0 °C | 419 J/(kg·K) Show Material materials with Specific heat capacity of 419 J/(kg·K) | ||
400.0 °C | 431 J/(kg·K) Show Material materials with Specific heat capacity of 431 J/(kg·K) | ||
500.0 °C | 444 J/(kg·K) Show Material materials with Specific heat capacity of 444 J/(kg·K) | ||
600.0 °C | 452 J/(kg·K) Show Material materials with Specific heat capacity of 452 J/(kg·K) | ||
700.0 °C | 456 J/(kg·K) Show Material materials with Specific heat capacity of 456 J/(kg·K) | ||
Thermal conductivity | -200.0 °C | 50 W/(m·K) Show Material materials with Thermal conductivity of 50 W/(m·K) | |
20.0 °C | 121 - 126 W/(m·K) Show Material materials with Thermal conductivity of 121 - 126 W/(m·K) | ||
200.0 °C | 147 W/(m·K) Show Material materials with Thermal conductivity of 147 W/(m·K) | ||
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 1.60E+7 - 1.70E+7 S/m Show Material materials with Electrical conductivity of 1.60E+7 - 1.70E+7 S/m |
Electrical resistivity | 200.0 °C | 7.7E-8 Ω·m Show Material materials with Electrical resistivity of 7.7E-8 Ω·m |
500.0 °C | 1.08E-7 Ω·m Show Material materials with Electrical resistivity of 1.08E-7 Ω·m | |
Specific Electrical conductivity | 28 - 29 % IACS Show Material materials with Specific Electrical conductivity of 28 - 29 % IACS |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.02 % Show Material materials with Aluminium of 0.02 % |
Copper | 69 - 71 % Show Material materials with Copper of 69 - 71 % |
Iron | 0.05 % Show Material materials with Iron of 0.05 % |
Lead | 0.05 % Show Material materials with Lead of 0.05 % |
Nickel | 0.3 % Show Material materials with Nickel of 0.3 % |
Tin | 0.1 % Show Material materials with Tin of 0.1 % |