EN 12166 Grade CuZn36 H02

Want to keep this datasheet? Save it now in your required format

Description

CuZn36 (CW507L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn33. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very good machinability: moderately hard soldering: good soft soldering: very good TIG-welding: moderately burnishing: very good CuZn36 is used for deep drawing components, pressure and punching components as well as for clockfaces. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.45 g/cm³

Show Material materials with Density of 8.45 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

110 GPa

Show Material materials with Elastic modulus of 110 GPa

100.0 °C

106 GPa

Show Material materials with Elastic modulus of 106 GPa

200.0 °C

102 GPa

Show Material materials with Elastic modulus of 102 GPa

300.0 °C

97 GPa

Show Material materials with Elastic modulus of 97 GPa

400.0 °C

89 GPa

Show Material materials with Elastic modulus of 89 GPa

500.0 °C

79 GPa

Show Material materials with Elastic modulus of 79 GPa

Hardness, Vickers

20.0 °C

155 - 190 [-]

Show Material materials with Hardness, Vickers of 155 - 190 [-]

Shear modulus

23.0 °C

40 GPa

Show Material materials with Shear modulus of 40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

550 - 750 MPa

Show Material materials with Tensile strength of 550 - 750 MPa

Yield strength Rp0.2

20.0 °C

550 - 610 MPa

Show Material materials with Yield strength Rp0.2 of 550 - 610 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

150.0 °C

1.9E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.9E-5 1/K

300.0 °C

2.1E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.1E-5 1/K

650.0 °C

2.3E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.3E-5 1/K

800.0 °C

2.4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.4E-5 1/K

Unlock all property charts

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Show Material materials with Specific heat capacity of 377 J/(kg·K)

Thermal conductivity

-200.0 °C

50 W/(m·K)

Show Material materials with Thermal conductivity of 50 W/(m·K)

20.0 °C

120 W/(m·K)

Show Material materials with Thermal conductivity of 120 W/(m·K)

200.0 °C

142 W/(m·K)

Show Material materials with Thermal conductivity of 142 W/(m·K)

Unlock all property charts

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.50E+7 S/m

Show Material materials with Electrical conductivity of 1.50E+7 S/m

200.0 °C

1.20E+7 S/m

Show Material materials with Electrical conductivity of 1.20E+7 S/m

Unlock all property charts

Electrical resistivity

20.0 °C

6.6E-8 Ω·m

Show Material materials with Electrical resistivity of 6.6E-8 Ω·m

200.0 °C

8.3E-8 Ω·m

Show Material materials with Electrical resistivity of 8.3E-8 Ω·m

Unlock all property charts

Chemical properties

PropertyValue

Aluminium

0.02 %

Show Material materials with Aluminium of 0.02 %

Copper

63.5 - 65 %

Show Material materials with Copper of 63.5 - 65 %

Iron

0.05 %

Show Material materials with Iron of 0.05 %

Lead

0.05 %

Show Material materials with Lead of 0.05 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Tin

0.1 %

Show Material materials with Tin of 0.1 %