EN 12166 Grade CuZn35Pb2 R480

Want to keep this datasheet? Save it now in your required format

Description

Material CuZn35Pb2, mat. No. CW601N, is an unhardenable wrought alloy. To the comparable make CuZn36Pb1,5, mat. No. 2.0331 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded brass grade of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: good cold forming: good machinability: very good hard soldering: moderately soft soldering: very good TIG-welding: unfavorable burnishing: very good Application: Wheels for circuit boards in watch industry, matrices for printing industry, clamps for electrical engineering, nipples, screws.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.46 - 8.5 g/cm³

Show Material materials with Density of 8.46 - 8.5 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

20.0 °C

105 - 110 GPa

Show Material materials with Elastic modulus of 105 - 110 GPa

Elongation

20.0 °C

8 %

Show Material materials with Elongation of 8 %

Elongation A100

20.0 °C

2 - 3 %

Show Material materials with Elongation A100 of 2 - 3 %

Elongation A11.3

20.0 °C

5 %

Show Material materials with Elongation A11.3 of 5 %

Shear modulus

20.0 °C

39 GPa

Show Material materials with Shear modulus of 39 GPa

Tensile strength

20.0 °C

480 MPa

Show Material materials with Tensile strength of 480 MPa

Yield strength Rp0.2

20.0 °C

350 MPa

Show Material materials with Yield strength Rp0.2 of 350 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

200.0 °C

2.04E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.04E-5 1/K

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

23.0 °C

371 - 418 J/(kg·K)

Show Material materials with Specific heat capacity of 371 - 418 J/(kg·K)

Typical for Wrought Copper Brass

Thermal conductivity

20.0 °C

113 - 116 W/(m·K)

Show Material materials with Thermal conductivity of 113 - 116 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.47E+7 S/m

Show Material materials with Electrical conductivity of 1.47E+7 S/m

Electrical resistivity

20.0 °C

6.8E-8 Ω·m

Show Material materials with Electrical resistivity of 6.8E-8 Ω·m

Specific Electrical conductivity

25 % IACS

Show Material materials with Specific Electrical conductivity of 25 % IACS

Chemical properties

PropertyValue

Aluminium

0.05 %

Show Material materials with Aluminium of 0.05 %

Copper

62 - 63.5 %

Show Material materials with Copper of 62 - 63.5 %

Iron

0.1 %

Show Material materials with Iron of 0.1 %

Lead

1.6 - 2.5 %

Show Material materials with Lead of 1.6 - 2.5 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Tin

0.1 %

Show Material materials with Tin of 0.1 %