EN 12166 Grade CuZn36Pb3 H04

Want to keep this datasheet? Save it now in your required format

Description

Material CuZn36Pb3, mat. No. CW603N, is an unhardenable wrought alloy. to the comparable make CuZn36Pb3, mat. No. 2.0375 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded brass grade of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: good cold forming: good machinability: very good hard soldering: moderately soft soldering: very good TIG-welding: unfavorable burnishing: very good Application: for thin-walled extruded profiles e.g. construction profiles, hand rails, for stair rails, for screw machine parts in watch and electrical industry as well as for precision mechanics and optics.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

100 - 125 GPa

Show Material materials with Elastic modulus of 100 - 125 GPa

Typical for Wrought Copper Brass

Elongation

20.0 °C

8 %

Show Material materials with Elongation of 8 %

Elongation A10

20.0 °C

6 %

Show Material materials with Elongation A10 of 6 %

Elongation A100

20.0 °C

3 %

Show Material materials with Elongation A100 of 3 %

Hardness, Vickers

20.0 °C

130 - 170 [-]

Show Material materials with Hardness, Vickers of 130 - 170 [-]

Shear modulus

23.0 °C

40 GPa

Show Material materials with Shear modulus of 40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

480 - 500 MPa

Show Material materials with Tensile strength of 480 - 500 MPa

Yield strength Rp0.2

20.0 °C

360 - 380 MPa

Show Material materials with Yield strength Rp0.2 of 360 - 380 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.7E-5 - 2.1E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K

Typical for Wrought Copper Brass

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

23.0 °C

371 - 418 J/(kg·K)

Show Material materials with Specific heat capacity of 371 - 418 J/(kg·K)

Typical for Wrought Copper Brass

Thermal conductivity

23.0 °C

100 - 234 W/(m·K)

Show Material materials with Thermal conductivity of 100 - 234 W/(m·K)

Typical for Wrought Copper Brass

Chemical properties

PropertyValue

Aluminium

0.05 %

Show Material materials with Aluminium of 0.05 %

Copper

60 - 62 %

Show Material materials with Copper of 60 - 62 %

Iron

0.3 %

Show Material materials with Iron of 0.3 %

Lead

2.5 - 3.5 %

Show Material materials with Lead of 2.5 - 3.5 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Tin

0.2 %

Show Material materials with Tin of 0.2 %