EN 12167 Grade CuZn40Pb2 H130

Want to keep this datasheet? Save it now in your required format

Description

Material CuZn40Pb2, mat. No. CW617N, is an unhardenable wrought alloy. to the comparable make CuZn40Pb2, mat. No. 2.0402 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn40. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: unfavorable machinability: very good hard soldering: moderately soft soldering: very good TIG-welding: unfavorable burnishing: very good Application: for hot-pressed components, turned parts for precision engineering and optics, circuit boards and clockwerks as well as for clamps for electrical engineering.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.4 - 8.44 g/cm³

Show Material materials with Density of 8.4 - 8.44 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

96 - 97 GPa

Show Material materials with Elastic modulus of 96 - 97 GPa

Hardness, Brinell

20.0 °C

130 [-]

Show Material materials with Hardness, Brinell of 130 [-]

Hardness, Vickers

20.0 °C

135 [-]

Show Material materials with Hardness, Vickers of 135 [-]

Shear modulus

23.0 °C

40 GPa

Show Material materials with Shear modulus of 40 GPa

Typical for Wrought Copper Brass

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

2E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2E-5 1/K

300.0 °C

2.1E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.1E-5 1/K

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Show Material materials with Specific heat capacity of 377 J/(kg·K)

Thermal conductivity

-200.0 °C

50 W/(m·K)

Show Material materials with Thermal conductivity of 50 W/(m·K)

20.0 °C

113 - 123 W/(m·K)

Show Material materials with Thermal conductivity of 113 - 123 W/(m·K)

Unlock all property charts

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.49E+7 - 1.50E+7 S/m

Show Material materials with Electrical conductivity of 1.49E+7 - 1.50E+7 S/m

200.0 °C

1.20E+7 S/m

Show Material materials with Electrical conductivity of 1.20E+7 S/m

Unlock all property charts

Electrical resistivity

20.0 °C

6.6E-8 Ω·m

Show Material materials with Electrical resistivity of 6.6E-8 Ω·m

200.0 °C

8.3E-8 Ω·m

Show Material materials with Electrical resistivity of 8.3E-8 Ω·m

Unlock all property charts

Specific Electrical conductivity

25.7 % IACS

Show Material materials with Specific Electrical conductivity of 25.7 % IACS

Chemical properties

PropertyValue

Aluminium

0.05 %

Show Material materials with Aluminium of 0.05 %

Copper

57 - 59 %

Show Material materials with Copper of 57 - 59 %

Iron

0.3 %

Show Material materials with Iron of 0.3 %

Lead

1.6 - 2.5 %

Show Material materials with Lead of 1.6 - 2.5 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Tin

0.3 %

Show Material materials with Tin of 0.3 %