EN 12167 Grade CuCo1Ni1Be R680

Want to keep this datasheet? Save it now in your required format

Description

The material CuCo1Ni1Be , mat. No CW103C is incomparable to a DIN-make. It is used in the form of plates, sheets, stripes, circular blanks, bars, prematerial for forged parts, wires, profiles and forged parts.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.3 - 8.8 g/cm³

Show Material materials with Density of 8.3 - 8.8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

110 - 130 GPa

Show Material materials with Elastic modulus of 110 - 130 GPa

Typical for Wrought Copper High Copper Alloy

Elongation

20.0 °C

10 %

Show Material materials with Elongation of 10 %

Elongation A100

20.0 °C

3 - 6 %

Show Material materials with Elongation A100 of 3 - 6 %

Elongation A11.3

20.0 °C

6 - 8 %

Show Material materials with Elongation A11.3 of 6 - 8 %

Tensile strength

20.0 °C

680 MPa

Show Material materials with Tensile strength of 680 MPa

Yield strength Rp0.2

20.0 °C

550 MPa

Show Material materials with Yield strength Rp0.2 of 550 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.6E-5 - 1.8E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K

Typical for Wrought Copper High Copper Alloy

Melting point

855 - 1090 °C

Show Material materials with Melting point of 855 - 1090 °C

Typical for Wrought Copper High Copper Alloy

Specific heat capacity

23.0 °C

360 - 420 J/(kg·K)

Show Material materials with Specific heat capacity of 360 - 420 J/(kg·K)

Typical for Wrought Copper High Copper Alloy

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

2.80E+7 S/m

Show Material materials with Electrical conductivity of 2.80E+7 S/m

Specific Electrical conductivity

48 % IACS

Show Material materials with Specific Electrical conductivity of 48 % IACS

Chemical properties

PropertyValue

Beryllium

0.4 - 0.7 %

Show Material materials with Beryllium of 0.4 - 0.7 %

Cobalt

0.8 - 1.3 %

Show Material materials with Cobalt of 0.8 - 1.3 %

Iron

0.2 %

Show Material materials with Iron of 0.2 %

Nickel

0.8 - 1.3 %

Show Material materials with Nickel of 0.8 - 1.3 %