Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 110 GPa Show Material materials with Elastic modulus of 110 GPa | |
50.0 °C | 110 GPa Show Material materials with Elastic modulus of 110 GPa | ||
100.0 °C | 108 GPa Show Material materials with Elastic modulus of 108 GPa | ||
150.0 °C | 107 GPa Show Material materials with Elastic modulus of 107 GPa | ||
200.0 °C | 106 GPa Show Material materials with Elastic modulus of 106 GPa | ||
250.0 °C | 105 GPa Show Material materials with Elastic modulus of 105 GPa | ||
Elongation | 20.0 °C | 55 % Show Material materials with Elongation of 55 % | |
Shear modulus | 23.0 °C | 40 GPa Show Material materials with Shear modulus of 40 GPa | Typical for Wrought Copper Brass |
Tensile strength | 20.0 °C | 340 MPa Show Material materials with Tensile strength of 340 MPa | |
Yield strength Rp0.2 | 20.0 °C | 120 MPa Show Material materials with Yield strength Rp0.2 of 120 MPa | |
Yield strength Rp1.0 | 20.0 °C | 130 MPa Show Material materials with Yield strength Rp1.0 of 130 MPa | |
50.0 °C | 130 MPa Show Material materials with Yield strength Rp1.0 of 130 MPa | ||
100.0 °C | 125 MPa Show Material materials with Yield strength Rp1.0 of 125 MPa | ||
150.0 °C | 125 MPa Show Material materials with Yield strength Rp1.0 of 125 MPa | ||
200.0 °C | 120 MPa Show Material materials with Yield strength Rp1.0 of 120 MPa | ||
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 - 2.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K | Typical for Wrought Copper Brass |
Melting point | 875 - 1075 °C Show Material materials with Melting point of 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 23.0 °C | 371 - 418 J/(kg·K) Show Material materials with Specific heat capacity of 371 - 418 J/(kg·K) | Typical for Wrought Copper Brass |
Thermal conductivity | 23.0 °C | 100 - 234 W/(m·K) Show Material materials with Thermal conductivity of 100 - 234 W/(m·K) | Typical for Wrought Copper Brass |
Chemical properties
Property | Value |
---|---|
Aluminium | 1.8 - 2.3 % Show Material materials with Aluminium of 1.8 - 2.3 % |
Arsenic | 0.02 - 0.06 % Show Material materials with Arsenic of 0.02 - 0.06 % |
Copper | 76 - 79 % Show Material materials with Copper of 76 - 79 % |
Iron | 0.07 % Show Material materials with Iron of 0.07 % |
Lead | 0.05 % Show Material materials with Lead of 0.05 % |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % |
Nickel | 0.1 % Show Material materials with Nickel of 0.1 % |
Phosphorus | 0.01 % Show Material materials with Phosphorus of 0.01 % |