EN 12451 Grade CuZn28Sn1As O60

View suppliers (1)
Want to keep this datasheet? Save it now in your required format

Description

CuZn28Sn1As (CW706R former identification: CuZn28Sn1) is an unhardenable copper alloy. High hardness and strength parameter are achievable by cold forming only. Tin increases corrosion resistance and improves sliding qualities. CuZn28Sn1As is dezincification resistant and resistant to river and industrial water. Processing properties: warm forming: good cold forming: moderately machinability: moderately hard soldering: moderately soft soldering: very good TIG-welding: good burnishing: very good This special brass material is predominantly applicated in the form of tubes for freshwater carrying pipes or for heat-exchanger. To the operating conditions applies that the content of solute substances in cooling water is not allowed to exceed 0,1% and the pH-value for water is not allowed to decrease below 7,0. In the case of corrosion attack due to sedimentations tubes made of CW706R are more resistant than tubes of binary copper-zinc alloys. The material is applicable for water speeds up to 2m/s. Further application for bottoms and plates for condenser and other heat-transformer, ribbed tubes as well as for cooler in on shore appliances.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.56 g/cm³

Show Material materials with Density of 8.56 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-253.0 °C

119 GPa

Show Material materials with Elastic modulus of 119 GPa

-195.0 °C

116 GPa

Show Material materials with Elastic modulus of 116 GPa

-100.0 °C

112 GPa

Show Material materials with Elastic modulus of 112 GPa

20.0 °C

108 - 110 GPa

Show Material materials with Elastic modulus of 108 - 110 GPa

50.0 °C

108 GPa

Show Material materials with Elastic modulus of 108 GPa

100.0 °C

108 GPa

Show Material materials with Elastic modulus of 108 GPa

150.0 °C

101 GPa

Show Material materials with Elastic modulus of 101 GPa

200.0 °C

94 GPa

Show Material materials with Elastic modulus of 94 GPa

250.0 °C

87 GPa

Show Material materials with Elastic modulus of 87 GPa

Elongation

20.0 °C

45 - 55 %

Show Material materials with Elongation of 45 - 55 %

Hardness, Vickers

20.0 °C

60 - 110 [-]

Show Material materials with Hardness, Vickers of 60 - 110 [-]

Shear modulus

20.0 °C

41 GPa

Show Material materials with Shear modulus of 41 GPa

Tensile strength

20.0 °C

320 - 360 MPa

Show Material materials with Tensile strength of 320 - 360 MPa

Yield strength Rp0.2

20.0 °C

100 - 140 MPa

Show Material materials with Yield strength Rp0.2 of 100 - 140 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

200.0 °C

1.95E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.95E-5 1/K

Melting point

875 - 1075 °C

Show Material materials with Melting point of 875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Show Material materials with Specific heat capacity of 377 J/(kg·K)

Thermal conductivity

20.0 °C

109 W/(m·K)

Show Material materials with Thermal conductivity of 109 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.41E+7 S/m

Show Material materials with Electrical conductivity of 1.41E+7 S/m

Electrical resistivity

20.0 °C

7.1E-8 Ω·m

Show Material materials with Electrical resistivity of 7.1E-8 Ω·m

Specific Electrical conductivity

24 % IACS

Show Material materials with Specific Electrical conductivity of 24 % IACS

Chemical properties

PropertyValue

Arsenic

0.02 - 0.06 %

Show Material materials with Arsenic of 0.02 - 0.06 %

Copper

70 - 72.5 %

Show Material materials with Copper of 70 - 72.5 %

Iron

0.07 %

Show Material materials with Iron of 0.07 %

Lead

0.05 - 0.07 %

Show Material materials with Lead of 0.05 - 0.07 %

Manganese

0.1 %

Show Material materials with Manganese of 0.1 %

Nickel

0.1 %

Show Material materials with Nickel of 0.1 %

Phosphorus

0.01 %

Show Material materials with Phosphorus of 0.01 %

Tin

0.9 - 1.3 %

Show Material materials with Tin of 0.9 - 1.3 %