Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.56 g/cm³ Show Material materials with Density of 8.56 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | -253.0 °C | 119 GPa Show Material materials with Elastic modulus of 119 GPa | |
-195.0 °C | 116 GPa Show Material materials with Elastic modulus of 116 GPa | ||
-100.0 °C | 112 GPa Show Material materials with Elastic modulus of 112 GPa | ||
20.0 °C | 108 - 110 GPa Show Material materials with Elastic modulus of 108 - 110 GPa | ||
50.0 °C | 108 GPa Show Material materials with Elastic modulus of 108 GPa | ||
100.0 °C | 108 GPa Show Material materials with Elastic modulus of 108 GPa | ||
150.0 °C | 101 GPa Show Material materials with Elastic modulus of 101 GPa | ||
200.0 °C | 94 GPa Show Material materials with Elastic modulus of 94 GPa | ||
250.0 °C | 87 GPa Show Material materials with Elastic modulus of 87 GPa | ||
Elongation | 20.0 °C | 45 % Show Material materials with Elongation of 45 % | |
Shear modulus | 23.0 °C | 40 GPa Show Material materials with Shear modulus of 40 GPa | Typical for Wrought Copper Brass |
Tensile strength | 20.0 °C | 360 MPa Show Material materials with Tensile strength of 360 MPa | |
Yield strength Rp0.2 | 20.0 °C | 140 MPa Show Material materials with Yield strength Rp0.2 of 140 MPa | |
Yield strength Rp1.0 | 20.0 °C | 150 MPa Show Material materials with Yield strength Rp1.0 of 150 MPa | |
50.0 °C | 150 MPa Show Material materials with Yield strength Rp1.0 of 150 MPa | ||
100.0 °C | 144 MPa Show Material materials with Yield strength Rp1.0 of 144 MPa | ||
150.0 °C | 140 MPa Show Material materials with Yield strength Rp1.0 of 140 MPa | ||
200.0 °C | 135 MPa Show Material materials with Yield strength Rp1.0 of 135 MPa | ||
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 - 2.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K | Typical for Wrought Copper Brass |
Melting point | 875 - 1075 °C Show Material materials with Melting point of 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 23.0 °C | 371 - 418 J/(kg·K) Show Material materials with Specific heat capacity of 371 - 418 J/(kg·K) | Typical for Wrought Copper Brass |
Thermal conductivity | 20.0 °C | 109 W/(m·K) Show Material materials with Thermal conductivity of 109 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 1.41E+7 S/m Show Material materials with Electrical conductivity of 1.41E+7 S/m |
Specific Electrical conductivity | 24 % IACS Show Material materials with Specific Electrical conductivity of 24 % IACS |
Chemical properties
Property | Value |
---|---|
Arsenic | 0.02 - 0.06 % Show Material materials with Arsenic of 0.02 - 0.06 % |
Copper | 70 - 72.5 % Show Material materials with Copper of 70 - 72.5 % |
Iron | 0.07 % Show Material materials with Iron of 0.07 % |
Lead | 0.05 % Show Material materials with Lead of 0.05 % |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % |
Nickel | 0.1 % Show Material materials with Nickel of 0.1 % |
Phosphorus | 0.01 % Show Material materials with Phosphorus of 0.01 % |
Tin | 0.9 - 1.3 % Show Material materials with Tin of 0.9 - 1.3 % |