General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.41 - 8.8 g/cm³ Show Material materials with Density of 8.41 - 8.8 g/cm³ |
Dimension
Property | Value | Comment |
---|---|---|
Diameter | 0.76 - 356 mm Show Material materials with Diameter of 0.76 - 356 mm | |
Length | 610 - 91000 mm Show Material materials with Length of 610 - 91000 mm | max. |
Outside diameter | 19.1 - 406 mm Show Material materials with Outside diameter of 19.1 - 406 mm | |
Thickness | 12.7 - 203.2 mm Show Material materials with Thickness of 12.7 - 203.2 mm | |
Width | 305 - 559 mm Show Material materials with Width of 305 - 559 mm |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 23.0 °C | 120 - 131 GPa Show Material materials with Elastic modulus of 120 - 131 GPa |
Elongation | 23.0 °C | 7.8 - 75 % Show Material materials with Elongation of 7.8 - 75 % |
Tensile strength | 23.0 °C | 410 - 750 MPa Show Material materials with Tensile strength of 410 - 750 MPa |
Yield strength | 23.0 °C | 600 MPa Show Material materials with Yield strength of 600 MPa |
Yield strength Rp0.2 | 23.0 °C | 130 - 250 MPa Show Material materials with Yield strength Rp0.2 of 130 - 250 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.75E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.75E-5 1/K |
Melting point | 870 °C Show Material materials with Melting point of 870 °C | |
Specific heat capacity | 23.0 °C | 410 J/(kg·K) Show Material materials with Specific heat capacity of 410 J/(kg·K) |
Thermal conductivity | 23.0 °C | 105 - 110 W/(m·K) Show Material materials with Thermal conductivity of 105 - 110 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 5.8E-6 - 6.9E-6 Ω·m Show Material materials with Electrical resistivity of 5.8E-6 - 6.9E-6 Ω·m |
Specific Electrical conductivity | 25 - 30 % IACS Show Material materials with Specific Electrical conductivity of 25 - 30 % IACS |
Magnetic
Property | Temperature | Value | Comment |
---|---|---|---|
Relative magnetic permeability | 23.0 °C | 1 [-] Show Material materials with Relative magnetic permeability of 1 [-] | max. |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 0 - 0.2 % Show Material materials with Aluminium of 0 - 0.2 % | |
Beryllium | 1.6 - 1.85 % Show Material materials with Beryllium of 1.6 - 1.85 % | |
Cobalt | 0.2 % Show Material materials with Cobalt of 0.2 % | min. Nickel + Cobalt |
Copper | 96.3 - 98.2 % Show Material materials with Copper of 96.3 - 98.2 % | Balance |
Iron | 0 - 0.6 % Show Material materials with Iron of 0 - 0.6 % | max., Nickel + Cobalt + Iron |
Nickel | 0.2 - 0.6 % Show Material materials with Nickel of 0.2 - 0.6 % | min. Nickel + Cobalt |
Other | 0 - 0.5 % Show Material materials with Other of 0 - 0.5 % | |
Silicon | 0 - 0.2 % Show Material materials with Silicon of 0 - 0.2 % |
Technological properties
Property | ||
---|---|---|
Application areas | Alloy 165 tube is used in crucial telecommunications applications including undersea instrument housings and repeater housings.,Typical applications include bushings, bearings and resistance welding components.,Typical applications include wear plates and resistance welding components. |