General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.83 - 8.9 g/cm³ Show Material materials with Density of 8.83 - 8.9 g/cm³ |
Dimension
Property | Value | Comment | |
---|---|---|---|
Diameter | 1.27 - 12.7 mm Show Material materials with Diameter of 1.27 - 12.7 mm | ||
Length | 610 - 91000 mm Show Material materials with Length of 610 - 91000 mm | max. Rod and Bar | |
Outside diameter | 0.76 - 406 mm Show Material materials with Outside diameter of 0.76 - 406 mm | Rod | |
Thickness | 0.05 - 254 mm Show Material materials with Thickness of 0.05 - 254 mm | Bar | |
Width | 1.27 - 559 mm Show Material materials with Width of 1.27 - 559 mm | ||
Wall thickness | Typically 10 to 20% of OD |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Bendability 90°, bw | 23.0 °C | 2 [-] Show Material materials with Bendability 90°, bw of 2 [-] | for strip with 0.25mm and thinner. |
Bendability 90°, gw | 23.0 °C | 1 [-] Show Material materials with Bendability 90°, gw of 1 [-] | for strip with 0.25mm and thinner. |
Elastic modulus | 23.0 °C | 120 - 138 GPa Show Material materials with Elastic modulus of 120 - 138 GPa | |
Elongation | 23.0 °C | 8 - 25 % Show Material materials with Elongation of 8 - 25 % | for strip with 0.1mm and thicker.,min. |
Hardness, Rockwell B | 23.0 °C | 92 - 100 [-] Show Material materials with Hardness, Rockwell B of 92 - 100 [-] | |
Hardness, Vickers | 23.0 °C | 195 - 275 [-] Show Material materials with Hardness, Vickers of 195 - 275 [-] | |
Tensile strength | 23.0 °C | 680 - 900 MPa Show Material materials with Tensile strength of 680 - 900 MPa | |
Yield strength Rp0.2 | 23.0 °C | 550 - 760 MPa Show Material materials with Yield strength Rp0.2 of 550 - 760 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.76E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.76E-5 1/K |
Melting point | 1030 - 1040 °C Show Material materials with Melting point of 1030 - 1040 °C | |
Specific heat capacity | 23.0 °C | 390 J/(kg·K) Show Material materials with Specific heat capacity of 390 J/(kg·K) |
Thermal conductivity | 23.0 °C | 210 - 240 W/(m·K) Show Material materials with Thermal conductivity of 210 - 240 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 2.9E-6 - 3.8E-6 Ω·m Show Material materials with Electrical resistivity of 2.9E-6 - 3.8E-6 Ω·m |
Specific Electrical conductivity | 45 - 60 % IACS Show Material materials with Specific Electrical conductivity of 45 - 60 % IACS |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 0 - 0.2 % Show Material materials with Aluminium of 0 - 0.2 % | |
Beryllium | 0.2 - 0.6 % Show Material materials with Beryllium of 0.2 - 0.6 % | |
Cobalt | 0 - 0.3 % Show Material materials with Cobalt of 0 - 0.3 % | |
Copper | 95.9 - 98.4 % Show Material materials with Copper of 95.9 - 98.4 % | Balance |
Iron | 0 - 0.1 % Show Material materials with Iron of 0 - 0.1 % | |
Nickel | 1.4 - 2.2 % Show Material materials with Nickel of 1.4 - 2.2 % | |
Other | 0 - 0.5 % Show Material materials with Other of 0 - 0.5 % | |
Silicon | 0 - 0.2 % Show Material materials with Silicon of 0 - 0.2 % |
Technological properties
Property | ||
---|---|---|
Application areas | Typical applications include high reliability spring contacts for switches and relays.,Typical applications for parts finished by forging or extrusion of these alloys include continuous casting mold components and resistance welding components.,Typical applications include resistance welding components, and inserts for metal die casting, injection molding and blow molding.,Typical applications include dies casting plunger tips and dies for steel extrusion.,Typical applications include heat exchanger tubing and resistance welding components.,Typical applications include coil springs and formed wire contacts. |