Property | Value | Temperature |
---|---|---|
Density | 8.36 - 8.8 g/cm³ Show Material materials with Density of 8.36 - 8.8 g/cm³ at 23.0 °C | 23.0 °C |
Dimension
Property | Value |
---|---|
Diameter | 1.27 - 12.7 mm Show Material materials with Diameter of 1.27 - 12.7 mm |
Mechanical
Property | Value | Temperature |
---|---|---|
Elastic modulus | 130 - 131 GPa Show Material materials with Elastic modulus of 130 - 131 GPa at 23.0 °C | 23.0 °C |
Elongation | 2 - 25 % Show Material materials with Elongation of 2 - 25 % at 23.0 °C | 23.0 °C |
Tensile strength | 620 - 1140 MPa Show Material materials with Tensile strength of 620 - 1140 MPa at 23.0 °C | 23.0 °C |
Yield strength | 1050 MPa Show Material materials with Yield strength of 1050 MPa at 23.0 °C | 23.0 °C |
Yield strength Rp0.2 | 510 - 730 MPa Show Material materials with Yield strength Rp0.2 of 510 - 730 MPa at 23.0 °C | 23.0 °C |
Thermal
Property | Value | Temperature |
---|---|---|
Coefficient of thermal expansion | 1.75E-5 - 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.75E-5 - 1.8E-5 1/K at 23.0 °C | 23.0 °C |
Melting point | 870 °C Show Material materials with Melting point of 870 °C | |
Specific heat capacity | 360 J/(kg·K) Show Material materials with Specific heat capacity of 360 J/(kg·K) at 23.0 °C | 23.0 °C |
Thermal conductivity | 105 - 110 W/(m·K) Show Material materials with Thermal conductivity of 105 - 110 W/(m·K) at 23.0 °C | 23.0 °C |
Electrical
Property | Value | Temperature |
---|---|---|
Electrical resistivity | 6.2E-6 - 7.8E-6 Ω·m Show Material materials with Electrical resistivity of 6.2E-6 - 7.8E-6 Ω·m at 23.0 °C | 23.0 °C |
Specific Electrical conductivity | 22 - 28 % IACS Show Material materials with Specific Electrical conductivity of 22 - 28 % IACS |
Chemical properties
Property | ||
---|---|---|
Aluminium | 0 - 0.2 % | |
Beryllium | 1.8 - 2 % | |
Cobalt | 0.2 % | min. Nickel + Cobalt |
Copper | 96.1 - 98 % | Balance |
Iron | 0 - 0.6 % | max., Nickel + Cobalt + Iron |
Nickel | 0.2 - 0.6 % | min. Nickel + Cobalt |
Other | 0 - 0.5 % | |
Silicon | 0 - 0.2 % |
Technological properties
Property | ||
---|---|---|
Application areas | Typical applications include precision coil springs and pins for burn-in and test socket contacts and probe pins, computer processor socket contacts, cold headed fasteners, modular jack contacts, woven mesh electromagnetic shielding gaskets and resilient eyeglass frames. |